Microtensile Bond Strenh Between Indirect Composite Resin Inlays and Dentin: Effect of Cementation Strategy and Mechanical Aging
Carregando...
Fonte externa
Fonte externa
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Quintessence Publishing Co Inc
Tipo
Artigo
Direito de acesso
Acesso restrito
Fonte externa
Fonte externa
Resumo
Purpose: To evaluate the microtensile bond strength of indirect resin composite inlays to dentin using two cementation strategies, before and after mechanical aging.Materials and Methods: Standardized inlay cavities (bucco-lingual width: 3 mm; depth: 4 mm) were prepared in 32 human premolars. The teeth were embedded in self-curing acrylic resin up to 3 mm from the cementoenamel junction, impressions were made using a polyvinyl siloxane material, master dies were obtained using type 4 stone, and inlay composite resin restorations were fabricated (Sinfony, 3M ESPE). The teeth were randomly allocated into 4 groups according to the cementation strategy (conventional [C] and simplified [S]) and aging (mechanical cycling [MC] and not aged): C[G1]: Adper Single Bond + RelyX ARC without aging; CMC[G2]: conventional cementation + mechanical cycling (10(6) cycles, 88 N, 4 Hz, 37 degrees C); S[G3]: self-adhesive resin cement (RelyX U-100) without aging; SMC[G4] self-adhesive cementation + mechanical cycling. Intaglio surfaces of composite inlays were treated by tribochemical silica coating in G1 and G2, while G3 and G4 received no surface treatment. Non-aged specimens were stored in a moist environment at ca 37 degrees C for the same period as MC (3 days). Non-trimmed beam specimens (bonding area = 1 mm(2)) were produced by serial cutting, and microtensile testing was performed (0.5 mm/min).Results: Two-way ANOVA showed that the microtensile bond strength was affected only by cementation strategy (p < 0.0001). Tukey's test showed that groups G1 (35.1 +/- 9.1) and G2 (32.7 +/- 10.7) presented significantly higher bond strength values than G3 (8.7 +/- 6.3) and G4 (5.2 +/- 4.6).Conclusion: The use of a conventional adhesive technique and tribochemical silica coating resulted in higher mu TBS than the one-step simplified cementation, even after mechanical cycling.
Descrição
Palavras-chave
adhesion, cementation, indirect resin, mechanical cycling, microtensile bond strength
Idioma
Inglês
Citação
Journal Of Adhesive Dentistry. Hanover Park: Quintessence Publishing Co Inc, v. 16, n. 4, p. 357-363, 2014.