Resumo
Objectives: the purpose of this study was to evaluate the surfaces of commercially pure titanium (cpTi) implants surface modified by laser beam (LS), by laser beam associated with sodium silicate deposition (SS) and compare them with surfaces modified by dual-acid etched (AS) and with machined surface (MS). Methods: thirty rabbits received two implants each (one for each tibia). After 30, 60 and 90 days postoperative, the implants were removed by reverse torque for biomechanical analysis and surfaces were analyzed by scanning electron microscopy (SEM) and X-ray energy dispersive spectroscopy (EDS). Results: the mean values of reverse torque at 30, 60 and 90 days postoperative were respectively 24.60, 43.60 e 60.40 N.cm to MS, 43.00, 68.20 e 63.80 N.cm to AS group, 59.80, 76.60 e 78.00 N.cm to LS group and 63.00, 75.40 e 76.60 N.cm to SS group. At 30 days, LS and SS groups showed statistically significant difference (p<0.05) compared to the other groups. At 60 days, LS and SS groups showed statistically significant difference (p<0.05) when compared to MS. Conclusions: it was concluded that SL and SS implants' biomechanical and topographical properties increased bone-implant interaction when compared to the AS and MS implants.
Descrição
Palavras-chave
Idioma
Inglês
Como citar
Journal of Dental Research, v. 89, 2010.