Publicação: Residues of different gel formulations on dentinal walls: a SEM/EDS analysis
Carregando...
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Artigo
Direito de acesso
Acesso restrito
Resumo
The aim of this study was to evaluate the presence of residues of sodium hypo-chlorite gel, chlorhexidine gel, and EDTA gel on dentina l walls after canal preparat ion throughchemical SEM- elemental chemical microanal ys is (EDS) analysis. Forty-eight single-rootedteeth were selected. They had their crowns sectioned and were instrumented with a reciprocat-ing system. The canals were irrigated with 5 mL of saline solution during root canal preparation.After instrumentation, the root canals were irrigated with 3 mL 17% EDTA followed by 1 min ofultrasonic passive activation (33 20 sec) to remove the smear layer, and then irrigated with3 mL of saline solution. The specimens were randomized into three groups (n 5 12) accord ing tothe chemical substance that filled the root canal for 30 min: GI: 5.5% sodium hypochlorite gel;GII: 2% chlorhexidine gel; GIII: 24% EDTA gel; Negative c ontrol group: no substance was used.Then, the root canals were irrigated with 6 mL of saline solution followed by 1 min of ultrasonicpassive activation (33 20 sec). After ultrasonic activation , the canals were irrigated with 2 mLsaline. The roots were sect ioned, and the perce ntage of each chemical element present in thesamples was analyzed through chemi cal SEM-EDS microanalysis. All expe rimental groupsshowed a significantly higher percentage of chemical elements (Na and/or Cl) than the controlgroup (P < 0.03). This in vitro study has shown that, regardless of chemical solutions used evenafter the final irrigation protocol, chemical residues of d ifferent substances remained attached tothe r oot c anal wa lls. Microsc. Res. Tech. 78:495–49 9, 2015.
Descrição
Palavras-chave
Endodontics, Sodium hypochlorite, Chlorhexidine, EDTA, Electron probe microanalysis
Idioma
Inglês
Como citar
Microscopy Research and Technique, v. 78, p. 495–499, 2015.