Publicação: Efficiency comparison of hyperbranched polymers as toughening agents for a one-part epoxy resin
Nenhuma Miniatura disponível
Data
2015-03-28
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Cambridge Univ Press
Tipo
Artigo
Direito de acesso
Acesso restrito
Resumo
A previously synthesized hyperbranched poly(butylene adipate) (HPBA) polymer was compared with a commercial dendritic polyol (HPOH) as a toughening agent for a commercial one-part epoxy resin. Both modifiers were added in weight percentages of 1, 3, 5, and 10%. The modified epoxies were characterized using differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), thermogravimetric analysis (TGA), melt rheological tests, and linear elastic fracture mechanics. Blend morphology and matrix-modifier interactions were evaluated using scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR) analysis, respectively. The toughness-improvement effect was achieved without substantial impairment of thermomechanical properties or degradation of the thermal stability of the epoxy resin. A meaningful decrease in viscosity was achieved with both modifiers, contributing to an easier infusion processability. No evidence of new chemical linking was found although phase separation was observed by SEM, leading to the conclusion that only interfacial linkage occurs between modifiers and epoxy chains. SEM analysis also clearly shows the fracture mode changing from brittle to ductile by addition of modifiers, which was more evident for blends of HPBA.
Descrição
Palavras-chave
Idioma
Inglês
Como citar
Journal Of Materials Research. New York: Cambridge Univ Press, v. 30, n. 6, p. 869-878, 2015.