Analyse titanium surface irradiated with laser, with and without deposited of durapatite
Data
2006-01-01
Autores
Sisti, Karin Ellen
Garcia JR., Idelmo Rangel [UNESP]
Guastaldi, Antonio Carlos [UNESP]
Antoniolli, Andréia C. M. B.
Rossi, Rafael De
Brochado Neto, Álvaro de L.
Título da Revista
ISSN da Revista
Título de Volume
Editor
Sociedade Brasileira para o Desenvolvimento da Pesquisa em Cirurgia
Resumo
OBJETIVO: Estudar a superfície de implantes osseointegráveis utilizando discos de titânio irradiados com feixe de laser. MÉTODOS: A amostra foi irradiada com feixes de laser de alta intensidade (Nd-YAG), posteriormente depositado hidróxiapatita e submetido a tratamento térmico. Foi analisada sob MEV (Microscópio Eletrônico de Varredura) e realizada análise morfológica qualitativa com microfotografias em vários aumentos. RESULTADOS: A superfície irradiada com laser apresentou deformidade superficial e característica isomórfica; a aplicação de hidroxiapatita pelo método de biomimético aumentou quantitativamente a área da superfície de titânio. CONCLUSÃO: A deposição de hidroxiapatita apresentou melhor característica isomórfica e aumento quantitativo da área superficial estudada, a amostra demonstrou características não encontradas nos implantes disposto no mercado.
PURPOSE: The aim of this study was to analyse the surface of titanium implants using disc irradiated with lasers. METHODS: Titanium discs were irradiated with laser high insensitive (Nd-YAG), deposited durapatite and used thermal treatment. Sample received qualitative morphological analyse trough micrographics with many size in SEM (Scanning Electron Microscopy). RESULTS: Surface laser irradiation shows roughness and isomorphic characteristic. The durapatite amplified the titanium surface area by method biomimetic. CONCLUSION: The surface treatment presented more deposition of durapatite, roughness on the surface, better isomorphic characteristic and increase quantitative in titanium surface area, samples shows rugous, roughness and homogeneity there is not found in the implants available at the market.
PURPOSE: The aim of this study was to analyse the surface of titanium implants using disc irradiated with lasers. METHODS: Titanium discs were irradiated with laser high insensitive (Nd-YAG), deposited durapatite and used thermal treatment. Sample received qualitative morphological analyse trough micrographics with many size in SEM (Scanning Electron Microscopy). RESULTS: Surface laser irradiation shows roughness and isomorphic characteristic. The durapatite amplified the titanium surface area by method biomimetic. CONCLUSION: The surface treatment presented more deposition of durapatite, roughness on the surface, better isomorphic characteristic and increase quantitative in titanium surface area, samples shows rugous, roughness and homogeneity there is not found in the implants available at the market.
Descrição
Palavras-chave
Lasers, Titânio, Durapatita, Lasers, Titanium, Durapatite
Como citar
Acta Cirúrgica Brasileira. Sociedade Brasileira para o Desenvolvimento da Pesquisa em Cirurgia, v. 21, p. 57-62, 2006.