Publicação: WC-CoCr coatings sprayed by high velocity oxygen-fuel (HVOF) flame on AA7050 aluminum alloy: electrochemical behavior in 3.5% NaCl solution
Carregando...
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
ABM, ABC, ABPol
Tipo
Artigo
Direito de acesso
Acesso aberto
Resumo
In the present work, the electrochemical behavior of WC-CoCr coatings with 10 (W10), 15 (W15) and 20 (W20) torch passes sprayed by High Velocity Oxygen-Fuel (HVOF) flame on AA7050 aluminum alloy substrate, evaluated in 3.5% NaCl solution, were compared using open-circuit potential (E OC) measurements, electrochemical impedance spectroscopy (EIS) and polarization curves. The coating surfaces and their cross sections were characterized by X ray diffraction and the Rockwell-C hardness test, and also by optical (OM) and scanning electron microscopy (SEM) before and after the corrosion tests. The electrochemical data showed that sample W10 presented higher corrosion resistance than the others in chloride solutions. In some tests, aluminum salts on the coating surface were identified by EDS, indicating the corrosion of the substrate. and using aluminon, aluminum ions were detected and analyzing the surface via stereomicroscopy, hydrogen bubbles were observed, both showing that the electrolyte reached the substrate and galvanic corrosion possibly occurred. The physical characterization showed that sample W10 presented a lower number of cracks and pores, justifying its higher corrosion resistance.
Descrição
Palavras-chave
corrosion resistance, EIS, HVOF, WC-CoCr, aluminum alloy
Idioma
Inglês
Como citar
Materials Research. ABM, ABC, ABPol, v. 10, n. 4, p. 377-385, 2007.