Caracterização elétrica de blocos varistores à base de SnO2
Carregando...
Data
2012-09-01
Autores
Brito, R. L.
Pessôa, P. A. P.
Vasconcelos, J. S.
Santos, L. P. S. dos
Rangel, J. H. G.
Longo, Elson [UNESP]
Sousa, V. C. de
Ramirez, M. A. [UNESP]
Oliveira, M. M.
Título da Revista
ISSN da Revista
Título de Volume
Editor
Associação Brasileira de Cerâmica
Resumo
Neste trabalho foi realizado um estudo das propriedades elétricas de blocos varistores à base de SnO2. Foram avaliadas a não linearidade destas cerâmicas por meio da caracterização tensão-corrente, bem como a altura, largura e os portadores de cargas por espectroscopia de impedância, além das energias de ativação. Os valores de α foram relativamente baixos sendo o maior valor de 6,3 para o sistema 98,65%SnO2.1,00%Co2O3.0,05%Nb2O5.0,05%Cr2O3.0,25%Pr2O3 (SCNCrPr). O sistema 98,65%SnO2.1,00%Co2O3.0,05%Nb2O5. 0,05%Cr2O3.0,25%La2O3 (SCNCrLa) apesar de apresentar um tamanho médio de grão pequeno 1,66 μm, possuiu um valor muito baixo de Er, o que pode está associado a não formação de barreiras efetivas na região de contorno de grão, gerando uma corrente de fuga elevada da ordem de 230 μA.
This paper reports on a study of the electrical properties of SnO2-based varistor blocks. The nonlinearity of these ceramics was evaluated based on their voltage-current characteristics, while the height, width and charge carriers were evaluated by impedance spectroscopy and activation energies. The α values were relatively low, with the SCNCrPr system showing the highest value: 6.3. Although the average grain size of the SCNCrLa system was small, i.e., 1.66 μm, its Er value was very low, which may be attributed to the non-formation of effective barriers in the grain boundary region, thus generating a high leakage current in the order of 230 μA.
This paper reports on a study of the electrical properties of SnO2-based varistor blocks. The nonlinearity of these ceramics was evaluated based on their voltage-current characteristics, while the height, width and charge carriers were evaluated by impedance spectroscopy and activation energies. The α values were relatively low, with the SCNCrPr system showing the highest value: 6.3. Although the average grain size of the SCNCrLa system was small, i.e., 1.66 μm, its Er value was very low, which may be attributed to the non-formation of effective barriers in the grain boundary region, thus generating a high leakage current in the order of 230 μA.
Descrição
Palavras-chave
propriedades elétricas, SnO2, varistores, electrical properties, SnO2, varistors
Como citar
Cerâmica. Associação Brasileira de Cerâmica, v. 58, n. 347, p. 349-356, 2012.