Effects of powder preparation and sintering procedure on microstructure and dielectric properties of PLZT ceramics
Carregando...
Arquivos
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Int Inst Science Sintering (i I S S)
Tipo
Artigo
Direito de acesso
Acesso aberto
Resumo
PLZT ceramics belong to one of the very important groups of functional materials that make a basis for the production of a large range of electronic devices. The microstructure and properties of ceramics depend on the powder preparation and thermal processing conditions. Various techniques have been used to obtain chemically homogeneous and fine starting powders. PLZT powders have been prepared by two different production routes: by a modified Pechini method, using a polymeric precursor method (PMM) and by a partial oxalate method. A two-step sintering process, including a hot pressing, was carried out at 1100 and 1200degreesC Distinct phases obtained during the sintering process have been investigated by SEM and EDS techniques and dielectric properties such as permittivity and dielectric loss were measured in a frequency range from 1 to 20 kHz.. A significant difference in microstructure and dielectric properties, depending on powder origin and sintering procedure, has been noticed.
Descrição
Palavras-chave
sintering, dielectric materials, microstructure
Idioma
Inglês
Citação
Science of Sintering. Belgrade: Int Inst Science Sintering (i I S S), v. 35, n. 3, p. 133-140, 2003.