Publicação: Ferroelectric properties of mechanically synthesized nanosized barium titanate
Nenhuma Miniatura disponível
Data
2005-01-01
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Taylor & Francis Ltd
Tipo
Artigo
Direito de acesso
Acesso restrito
Resumo
Barium titanate ceramics were prepared through mechanochemical synthesis starting from fresh prepared barium oxide and titanium oxide in rutile form. Mixture of oxides was milled in zirconia oxide jar in the planetary ball-mill during 30, 60, 120 and 240 min. Extended time of milling directed to formation of higher amount of barium titanate perovskite phase. Barium titanate with good crystallinity was formed after 240 min. Sintering without pre-calcinations step was performed at 1330 degrees C for 2 hours with heating rate of 10 degrees C/min. The XRD, DSC, IR and TEM analyses were performed. Electric and ferroelectric properties were studied. Very well defined hysteresis loop was obtained.
Descrição
Idioma
Inglês
Como citar
Ferroelectrics. Abingdon: Taylor & Francis Ltd, v. 319, p. 65-73, 2005.