alpha-SiAlON ceramics with elongated grain morphology using an alternative sintering additive
Carregando...
Fonte externa
Fonte externa
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Elsevier B.V.
Tipo
Artigo
Direito de acesso
Acesso restrito
Fonte externa
Fonte externa
Resumo
In this work, the use of a natural yttrium oxide and rare earth oxide solid solution (CRE2O3) as stabilizers of the alpha-Si3N4 phase to form alpha-SiAlON has been investigated. This oxide mix is produced at FAENQUIL-DEMAR, at a cost of only 20% of pure commercial Y2O3. Two alpha-SiAlONs using pure Y2O3 or CRE2O3 have been prepared, using mixes of 20% by volume of a molar fraction of 9:1 of AlN to Y2O3 or AlN to CRE2O3, respectively, with 80% alpha-Si3N4. Samples were gas pressure-sintered at 1900 degreesC, under 1.5 MPa of N-2 for 60 min. Both compositions yielded alpha-SiAlON ceramics with high relative densities (98% t.d.), hardness of 18 GPa and fracture toughness of 5 Mpa m(1/2), with homogeneous microstructures composed of elongated alpha-SiAlON grains with aspect ratios of 5. It is concluded that the mixed rare earth concentrate (CRE2O3) can be used to produce alpha-SiAlON ceramics with similar microstructures and mechanical properties of alpha-SiAlON ceramics fabricated using pure Y2O3, but with the advantage of its lower production cost. (C) 2004 Elsevier B.V All rights reserved.
Descrição
Palavras-chave
sintering additive, alpha-SiAlON, microstructure, mechanical properties
Idioma
Inglês
Citação
Materials Letters. Amsterdam: Elsevier B.V., v. 58, n. 11, p. 1792-1796, 2004.