Publicação:
Effect of cobalt(II) oxide and manganese(IV) oxide on sintering of tin(IV) oxide

Nenhuma Miniatura disponível

Data

1996-03-01

Autores

Orientador

Coorientador

Pós-graduação

Curso de graduação

Título da Revista

ISSN da Revista

Título de Volume

Editor

Tipo

Artigo

Direito de acesso

Acesso restrito

Resumo

Additions of 0.5 to 2.0 mol% of CoO or MnO2 onto SnO, promote densification of this oxide up to 99% of theoretical density. The temperature of the maximum shrinkage rate (TM) and the relative density in the maximum densification rate (p*) during constant sintering heating rate depend on the dopant concentration. Thus, dopant concentration controls the densifying and nondensifying mechanisms during sintering. The densification of SnO2 witih addition of CoO or MnO, is explained in terms of the creation of oxygen vacancies.

Descrição

Palavras-chave

Additives, Cobalt compounds, Composition effects, Densification, Manganese compounds, Oxygen, Shrinkage, Sintering, Temperature, Cobalt oxide, Dopant concentration, High density ceramic bodies, Manganese oxide, Oxygen vacancies, Tin oxide, Tin compounds

Idioma

Inglês

Como citar

Journal of the American Ceramic Society, v. 79, n. 3, p. 799-804, 1996.

URI

http://hdl.handle.net/11449/64748

Itens relacionados

Financiadores

Coleções

Araraquara - IQAR - Instituto de Química

Unidades

Departamentos

Cursos de graduação

Programas de pós-graduação