Publicação: Effect of ceramic surface treatment on the microtensile bond strength between a resin cement and an alumina-based ceramic
Nenhuma Miniatura disponível
Data
2004-12-01
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Artigo
Direito de acesso
Acesso restrito
Resumo
Purpose: The objective of this study was to test the following hypothesis: the silica coating on ceramic surface increases the bond strength of resin cement to a ceramic. Materials and Methods: In-Ceram Alumina blocks were made and the ceramic surface was treated: G1 - sandblasting with 110-μm aluminum oxide particles; G2 - Rocatec System: tribochemicai silica coating (Rocatec-Pre powder + Rocatec-Plus powder + Rocatec-Sil); G3 - CoJet System: silica coating (CoJet-Sand) + ESPE-Sil. The ceramic blocks were cemented to composite blocks with Panavia F resin cement (under a load of 750 g/1 min). The cemented blocks were stored in distilled water at 37°C for 7 days and sectioned along the x and y axes with a diamond disk. Samples with an adhesive area of ca 0.8 mm 2 (n = 45) were obtained. The samples were attached to an adapted device for the microtensile test, which was performed in a universal testing machine (EMIC) at a crosshead speed of 1 mm/min. Results: The obtained results were submitted to ANOVA and Tukey's test. Mean values of tensile strength (MPa) and standard deviation values were: (G1) 16.8 ± 3.2; (G2) 30.6 ± 4.5; (G3) 33.0 ± 5.0. G2 and 63 presented greater tensile strength than G1. There was no significant difference between G2 and G3. All the failures took place at the ceramic/resin cement interface. Conclusion: The silica coating (Rocatec or CoJet systems) of the ceramic surface increased the bond strength between the Panavia F resin cement and alumina-based ceramic.
Descrição
Palavras-chave
Aluminous ceramic, Bond strength, Microtensile test, Silica coating, Surface treatment, aluminum oxide, resin, silicon dioxide, tooth cement, ceramic prosthesis, tensile strength, Analysis of Variance, Dental Bonding, Dental Cements, Dental Porcelain, Dentin-Bonding Agents, Materials Testing, Resin Cements, Silicon Dioxide, Surface Properties, Tensile Strength
Idioma
Inglês
Como citar
Journal of Adhesive Dentistry, v. 6, n. 4, p. 327-332, 2004.