Diffuse Effect of the Tungsten Doped Ba(Zr0.10Ti0.90)O3 Ferroelectric Ceramics
Nenhuma Miniatura disponível
Data
2009-12-01
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Trabalho apresentado em evento
Direito de acesso
Acesso aberto![Acesso Aberto](assets/repositorio/images/logo_acesso_aberto_simples.png)
![Acesso Aberto](assets/repositorio/images/logo_acesso_aberto_simples.png)
Resumo
Barium zirconate titanate Ba(Ti0.90Zr0.10)O3 ceramics doped with WO<inf>3</inf> (BZT:2W) have been prepared by a traditional solid phase reaction. The effect of temperature on the structural and electrical properties was investigated. X ray diffraction data evidenced formation of secondary phases for the samples sintered at 1300oC end 1350oC while the pure phase was attained at 1200oC. A modified Curie-Weiss law was used to describe the diffuseness of a phase transition. As temperature increases, the maximum dielectric permittivity decreased. The fine-grained sample showed a 'diffuse-like' ferroelectric behavior. The dielectric permittivity reaches a maximum value (εm ~6420 at 10 kHz) for the ceramics sintered at 1200oC for 4 hours.
Descrição
Palavras-chave
Barium zirconate titanates , Dielectric permittivities , Effect of temperature , Ferroelectric behavior , Solid phase reaction , Structural and electrical properties , Temperature increase , X-ray diffraction data , Barium zirconate , Electric properties , Exhibitions , Ferroelectric ceramics , Permittivity , Sintering , X ray diffraction , Zirconium , Ceramic materials