Bond strength of a composite resin to an adhesive luting cement
Carregando...
Arquivos
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Artigo
Direito de acesso
Acesso aberto
Resumo
This study evaluated the influence of surface treatment on the shear bond strength of a composite resin (CR), previously submitted to the application of a temporary cement (TC), to an adhesive luting cement. Eight-four CR cylinders (5 mm diameter and 3 mm high) were fabricated and embedded in acrylic resin. The sets were divided into 6 groups (G1 to G6) (n=12). Groups 2 to 6 received a coat of TC. After 24 h, TC was removed and the CR surfaces received the following treatments: G2: ethanol; G3: rotary brush and pumice; G4: air-abrasion; G5: air-abrasion and adhesive system; G6: air-abrasion, acid etching and adhesive system. G1 (control) did not receive TC or any surface treatment. The sets were adapted to a matrix and received an increment of an adhesive luting cement. The specimens were subjected to the shear bond strength test. ANOVA and Tukey's tests showed that G3 (8.53 MPa) and G4 (8.63 MPa) differed significantly (p=0.001) from G1 (13.34 MPa). The highest mean shear bond strength values were found in G5 (14.78 MPa) and G6 (15.86 MPa). Air-abrasion of CR surface associated with an adhesive system provided an effective bond of the CR to the adhesive luting cement, regardless the pre-treatment with the phosphoric acid.
Descrição
Palavras-chave
Bond strength, Composite resin, Dental air abrasion, Resin cement, resin, tooth cement, analysis of variance, comparative study, dental bonding, dental care, dental surgery, methodology, nonparametric test, shear strength, surface property, Air Abrasion, Dental, Analysis of Variance, Composite Resins, Dental Bonding, Dental Cements, Dental Restoration, Temporary, Dental Stress Analysis, Light-Curing of Dental Adhesives, Shear Strength, Statistics, Nonparametric, Surface Properties
Idioma
Inglês
Citação
Brazilian Dental Journal, v. 21, n. 4, p. 322-326, 2010.