Publicação: Use of high energy ball milling on the sintering optimization of alumina ceramics
Nenhuma Miniatura disponível
Data
2010-12-15
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Tipo
Trabalho apresentado em evento
Direito de acesso
Acesso aberto
Resumo
In this work, the effect of the milling time on the densification of the alumina ceramics with or without 5wt.%Y 2O 3, is evaluated, using high-energy ball milling. The milling was performed with different times of 0, 2, 5 or 10 hours. All powders, milled at different times, were characterized by X-Ray Diffraction presenting a reduction of the crystalline degree and crystallite size as function of the milling time increasing. The powders were compacted by cold uniaxial pressing and sintered at 1550°C-60min. Green density of the compacts presented an increasing as function of the milling time and sintered samples presented evolution on the densification as function of the reduction of the crystallite size of the milled powders. © (2010) Trans Tech Publications.
Descrição
Palavras-chave
Al 2O 3, Al 2O 3-Y 2O 3, Characterization, High-energy ball milling, Sintering, Alumina ceramic, Cold uniaxial pressings, Crystalline degree, Green densities, Milled powders, Milling time, Sintered samples, Aluminum, Ceramic materials, Crystallite size, High energy physics, Milling (machining), Milling machines, Powders, Sintered alumina, Spheres, X ray diffraction, X ray powder diffraction, Ball milling
Idioma
Inglês
Como citar
Materials Science Forum, v. 660-661, p. 701-706.