High-pressure assisted sintering of Ti-20Si-10B and Ti-10Si-5B powders
Nenhuma Miniatura disponível
Data
2012-11-26
Autores
Pereira, Wladimir Leite
Trindade Ramos, Erika Coaglia
Ramos, Alfeu Saraiva [UNESP]
Silva, Alexandro Nakano
Caetano Lima, Filipe Tavares
Filgueira, Marcello
Título da Revista
ISSN da Revista
Título de Volume
Editor
Resumo
This work presents the structural characterization of Ti-10Si-5B and Ti-20Si-10B (at-%) alloys produced by high-pressure assisted sintering. Sintering was performed in air at 1100 and 1200°C for 60 s using pressure levels of 5 GPa. Structural evaluation of sintered samples was conducted by means of scanning electron microscopy and energy dispersive spectrometry. Samples were successfully consolidated after sintering, which presented theoretical density values higher than 99%. The microstructures of the sintered Ti-10Si-5B and Ti-20Si-10B alloys revealed the presence of the TiSS, TiB, TiB2, Ti5Si3, Ti5Si4, TiSi, and TiSi2.phases. A small amount of Ti6Si2B was formed after high-pressure assisted sintering of the Ti-20Si-10B alloy (5GPa, 1100°C for 60 s) indicating that equilibrium structures were not achieved during short sintering times. No oxygen and carbon contamination was detected in structures of Ti-Si-B alloys after high-pressure sintering at 1100 and 1200°C without controlled atmosphere. © (2012) Trans Tech Publications, Switzerland.
Descrição
Palavras-chave
Electron microscope, Powder metallurgy, Sintering, Titanium alloys, Carbon contamination, Energy dispersive spectrometry, Equilibrium structures, High pressure sintering, Pressure level, Sintered samples, Structural characterization, Structural evaluation, Theoretical density, Alloys, Electron microscopes, Scanning electron microscopy, Silicon, Titanium compounds
Como citar
Materials Science Forum, v. 727-728, p. 462-467.