Correlation between hybrid layer thickness, resin tag length and microtensile bond strength of a self-etching adhesive system

Nenhuma Miniatura disponível

Data

2012-12-01

Autores

Rahal, Vanessa [UNESP]
Oliveira, Fernanda G. de [UNESP]
Briso, André Luiz Fraga [UNESP]
Santos, Paulo Henrique dos [UNESP]
Sundefeld, Maria Lúcia Marçal Mazza [UNESP]
Sundfeld, Renato Herman [UNESP]

Título da Revista

ISSN da Revista

Título de Volume

Editor

Resumo

The purpose of this study was to evaluate the correlation between the hybrid layer thickness, resin tag length and resin bond strength of a self-etching adhesive system to sound dentin tissue in vivo. After performing restorative procedures and tooth extractions, ten specimens were sectioned in a mesiodistal direction. One dental section was used for light microscope analysis, in which both the resin tag length and hybrid layer thickness were measured, while the other section was analyzed using a microtensile test (0.5 mm/min). The fractured surface of the latter section was characterized using a stereoscopic magnifying glass (40x magnifcation). The results were subject to statistical analysis using the Pearson Correlation Test (a = 0.05). The hybrid layer thickness, resin tag length and resin bond strength mean values were 2.19 microm (0.34), 4.34 microm (0.28) and 9.73 MPa (5,55), respectively. In addition, correlation tests between the resin tag length and the resin bond strength (r=0.014) and also between the hybrid layer thickness and bond strength (r=0.43), showed no statistically significant correlation. The microtensile bond strength of Adper Prompt L Pop self-etching adhesive system does not depend on hybrid layer thickness or resin tag length.

Descrição

Palavras-chave

resin, tooth cement, dental bonding, dental etching, human, in vitro study, materials testing, surface property, tensile strength, Dental Bonding, Dental Cements, Dental Etching, Humans, Materials Testing, Resins, Synthetic, Surface Properties, Tensile Strength

Como citar

Acta odontológica latinoamericana : AOL, v. 25, n. 2, p. 231-237, 2012.