Caracterização de materiais experimentais e comerciais para reembasamento imediato por meio de análise de propriedades físico-químicas e mecânicas

Página do item simplificado
dc.contributor.advisorVergani, Carlos Eduardo [UNESP]
dc.contributor.authorReis, José Mauricio dos Santos Nunes [UNESP]
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2014-06-11T19:35:01Z
dc.date.available2014-06-11T19:35:01Z
dc.date.issued2009-07-03
dc.description.abstractEste estudo avaliou o comportamento exotérmico de 5 resinas rígidas para reembasamento imediato, duas experimentais (E1 e E2) à base de agentes de ligação cruzada (etileno glicol dimetacrilato e 1,4-butanediol dimetacrilato) e três comerciais (Kooliner-K, New Truliner-NT, Tokuyama Rebase II-TR II), bem como o grau de conversão (GC), a sorção (Sor) e a solubilidade (Sol) em água, a contração linear de polimerização (CLP), as propriedades viscoelásticas e a resistência à flexão desses materiais e de uma resina para base de prótese (Lucitone 550-L). Foi avaliada, ainda, a resistência de união (RU) entre os reembasadores e a resina de base. O comportamento exotérmico foi avaliado (n=4) com termopar tipo K inserido no interior das resinas, em matriz circular (60 x 2,0 mm), e mantido até a polimerização. O GC (%) foi avaliado (n=5) por espectroscopia de infravermelho por transformadas de Fourier (32 leituras; resolução 4,0 cm-1). A Sor e a Sol (μg/mm3) foram mensuradas (n=5) seguindo as recomendações da ISO 1567. A CLP (%) foi avaliada (n=10), em projetor de perfil (Nikon 6C), em corpos-de-prova circulares (50 x 0,5 mm). Para avaliar as propriedades viscoelásticas, corpos-de-prova (40 x 10 x 3,3 mm) foram submetidos (n=2) à análise térmica dinâmico-mecânica (DMTA) em diferentes intervalos de temperatura (ciclos). O módulo de armazenamento (E’) e o amortecimento mecânico (tan δ) a 37ºC foram registrados durante o primeiro e último ciclo da DMTA. A temperatura de transição vítrea (Tg) foi mensurada somente no último ciclo da DMTA. Os ensaios mecânicos de flexão (0,5 mm/min) foram realizados (n=10) em corpos-de-prova (64 x 10 x 3,3 mm) intactos ou reembasados e a resistência (MPa) calculada na tensão máxima (RFM) e no limite de proporcionalidade (RFLP). Para avaliar a RU (MPa) entre os materiais, 60 cilindros (20 x 20 mm) da resina L foram processados...pt
dc.description.abstractThis study evaluated the exothermic behavior, degree of conversion (DC), water sorption (WSor), water solubility (WSol), linear polymerization shrinkage (LPS), viscoelastic properties and flexural strength of 5 hard chairside reline resins, two experimental (E1 and E2) based on crosslinking agents (ethylene glycol dimethacrylate and 1,4-butanediol dimethacrylate) and three commercially available (Kooliner-K, New Truliner-NT and Tokuyama Rebase II-TR II), and one heat-polymerized denture base resin (Lucitone 550-L). The shear bond strength (SBS) between the denture base resin and the reline materials was also evaluated. The exothermic behavior of circular specimens (60 x 2.0 mm) during polymerization was assessed (n=4) using a type K thermocouple. The DC (%) was measured (n=5) by Fourier Transformed infrared-attenuated total reflectance (FTIR-ATR) spectroscopy (32 scans; resolution of 4.0 cm-1). WSor and Wsol (μg/mm3) were determined (n=5) according to the recommendation stated in ISO 1567. The LPS (%) was measured (n=10) in circular specimens (50 x 0.5 mm) using a perfilometer (Nikon 6C). The viscoelastic properties of the specimens (40 x 10 x 3.3 mm) were evaluated (n=2) by dynamical-mechanical thermal analysis (DMTA) under different temperature ranges (runs). Values of storage modulus (E’) and loss tangent (tan δ) at 37ºC were obtained from the first and last runs. The glass transition temperature (Tg) was only measured from the last run. Ultimate flexural strength (UFS - MPa) and flexural strength at the proportional limit (FSPL - MPa) were determined (n=10) by three-point test (0.5 mm/min) using intact and relined specimens (64 x 10 x 3.3 mm). To evaluate the SBS between the materials, 60 cylinders (20 x 20 mm) of the denture base resin L were processed, relined (3.5 x 5.0 mm) and submitted to shear testing (0.5 mm/min). Data were analyzed by ANOVA and Tukey... (Complete abstract click electronic access below)en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.format.extent238 f. : il.
dc.identifier.aleph000598386
dc.identifier.capes33004030082P3
dc.identifier.citationREIS, José Mauricio dos Santos Nunes. Caracterização de materiais experimentais e comerciais para reembasamento imediato por meio de análise de propriedades físico-químicas e mecânicas. 2009. 238 f. Tese (doutorado) - Universidade Estadual Paulista, Faculdade de Odontologia de Araraquara, 2009.
dc.identifier.filereis_jmsn_dr_arafo.pdf
dc.identifier.lattes3003130522427820
dc.identifier.orcid0000-0002-7375-4714
dc.identifier.urihttp://hdl.handle.net/11449/105487
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.sourceAleph
dc.subjectResinas acrilicaspt
dc.subjectSolubilidadept
dc.subjectResistência ao cisalhamentopt
dc.subjectGrau de conversãopt
dc.subjectReembasadores de dentadurapt
dc.subjectDenture rebasingen
dc.subjectAcrylic resinsen
dc.subjectDenture linersen
dc.subjectSolubilityen
dc.subjectDegree of conversionen
dc.titleCaracterização de materiais experimentais e comerciais para reembasamento imediato por meio de análise de propriedades físico-químicas e mecânicaspt
dc.typeTese de doutorado
unesp.advisor.lattes3003130522427820[1]
unesp.advisor.orcid0000-0002-7375-4714[1]
unesp.campusUniversidade Estadual Paulista (Unesp), Faculdade de Odontologia, Araraquarapt
unesp.graduateProgramReabilitação Oral - FOARpt
unesp.knowledgeAreaPrótesept
unesp.researchAreaReabilitação oralpt

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
reis_jmsn_dr_arafo.pdf
Tamanho:
1.25 MB
Formato:
Adobe Portable Document Format
Baixar

Coleções

Teses - Reabilitação Oral - FOAR