Resistência à flexão biaxial, rugosidade e dureza de zircônias monolíticas: efeito da infiltração de sílica pelo método sol-gel e da simulação do desgaste fisiológico

Página do item simplificado
dc.contributor.advisorMarinho, Renata Marques de Melo [UNESP]
dc.contributor.advisorCampos, Tiago Moreira Bastos [UNESP]
dc.contributor.authorAlves, Larissa Marcia Martins [UNESP]
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2017-01-26T14:00:19Z
dc.date.available2017-01-26T14:00:19Z
dc.date.issued2016-12-20
dc.description.abstractEste estudo avaliou as propriedades mecânicas (resistência à flexão biaxial e dureza) e de superfície (rugosidade) da zircônia monolítica infiltrada com sílica, glazeada, ou polida. Foram confeccionados 198 discos de zircônia (14 mm de diâmetro, 1,2 mm de espessura). As amostras foram polidas com lixas de SiC #1200 e divididas em três grupos principais (n=66). No primeiro, os discos foram infiltrados com sílica, no segundo foram glazeados e no terceiro foram polidos com borrachas abrasivas. Após isso, foram divididos em dois subgrupos (n=33), nos quais somente um de cada tratamento foi submetido a simulação do desgaste fisiológico com esteatitas. Em seguida, as amostras foram submetidas a análises de rugosidade, dureza e ao ensaio de flexão biaxial (ISO 6872) em água. Também foram realizadas análises de difração de raios-X. Os valores de resistência (MPa) foram ranqueados e submetidos a análise de Weibull para cálculo de módulo e resistência característica dos materiais (IC 95%). As amostras também foram analisadas em microscopia eletrônica de varredura para a visualização do desgaste. Os difractrogramas mostraram que os tratamentos, glaze e infiltrado não induziram a transformação de fase, assim como o desgaste, porém o polimento induziu a formação de uma fase cúbica comprimida na superfície. A MEV mostrou as superfícies das amostras, com a formação de estrias nas amostras polidas, silicato de zircônia nas infiltradas e irregularidades nas glazeadas. Também foi possível verificar a remoção do tratamento de superfície após a simulação do desgaste. O glaze apresentou rugosidade e dureza superior, com diferença significativa, comparado aos demais tratamentos, quando não houve desgaste. Nos grupos com desgaste não houve diferença significativa. Nos resultados do teste de flexão, o grupo que apresentou a maior média foi o polido sem desgaste e após a realização da análise de Weibull, não houve diferença significativa entre eles.pt
dc.description.abstractThis study evaluated the mechanical properties (biaxial flexural strength and hardness) and surface properties (roughness) of infiltrated, glazed or polished monolithic zirconia. 198 zirconia discs were prepared (14 mm diameter, 1,2 mm thickness). The specimens were polished with SiC abrasive paper #1200, and then specimens were divided into three main groups (n=66). In the first, the discs were infiltrated with silica, in the second were glazed and and in third were polished with abrasive rubbers. Thereon, were divided into two subgroups (n=33), in which only one group of each treatment was subjected to wear with steatite, in order to simulate the physiological wear. The specimens were then subjected to roughness analysis, hardness and biaxial bending test (ISO 6872) immersed in water. The groups were evaluated by x-ray diffraction (XRD). The strength values (MPa) were ranked and subjected to Weibull analysis to calculate the Weibull modulus and characteristic strength of the material (CI 95%). The samples were also analyzed by SEM to visualize the wear. In the XRD, it was showed that the treatments did not induce phase transformation as well as wear, however the polishing induced the formation of a compressed cubic phase on the surface. SEM showed the surfaces of the samples with grooves formation on polished, zirconium silicate on infiltrated and irregularities on glazed. It was also possible to verify the removal of surface treatment after simulated wear. The glaze showed higher roughness amd hardness, with a significant difference compared to the other treatments, when there was no wear. In groups with wear there was no significant difference. The results of the bending test, the group with the highest average was polished without wear and after the Weibull analysis, there was no significant difference among them.en
dc.description.sponsorshipFundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)
dc.description.sponsorshipIdFAPESP: 2015/11405-7
dc.identifier.aleph000878919
dc.identifier.capes33004145070P8
dc.identifier.lattes3290027572731981
dc.identifier.orcid0000-0003-0752-6294
dc.identifier.urihttp://hdl.handle.net/11449/148610
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.subjectMateriais dentáriospt
dc.subjectCerâmicapt
dc.subjectZircôniapt
dc.subjectDurezapt
dc.subjectRugosidadept
dc.subjectDental materialsen
dc.subjectCeramicsen
dc.subjectZirconiaen
dc.subjectHardnessen
dc.subjectRoughnessen
dc.titleResistência à flexão biaxial, rugosidade e dureza de zircônias monolíticas: efeito da infiltração de sílica pelo método sol-gel e da simulação do desgaste fisiológicopt
dc.title.alternativeBiaxial flexural strength, roughness and hardness of monolithic zirconias: effect of silica infiltration by sol-gel method and physiological wear simulationen
dc.typeDissertação de mestrado
unesp.advisor.lattes3290027572731981[1]
unesp.advisor.orcid0000-0003-0752-6294[1]
unesp.campusUniversidade Estadual Paulista (Unesp), Instituto de Ciência e Tecnologia, São José dos Campospt
unesp.embargoOnlinept
unesp.graduateProgramOdontologia Restauradora - ICTpt
unesp.knowledgeAreaPrótese dentáriapt
unesp.researchAreaDesenvolvimento de Materiais e Novas Tecnologias em Odontologiapt

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
alves_lmm_me_bauru.pdf
Tamanho:
4.8 MB
Formato:
Adobe Portable Document Format
Descrição:
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
3.08 KB
Formato:
Item-specific license agreed upon to submission
Descrição:

Coleções

Dissertações - Odontologia Restauradora - ICT