dc.description.abstractGrain refinement of low carbon steel via the warm deformation of martensite during torsion testing was investigated. At the beginning of straining, laths with high dislocation density were observed. After large deformations, a ferrite matrix with grain size close to 1μm and dispersed cementite particles were attained.en
dc.description.affiliationUniversidade Estadual Paulista (UNESP), Ilha Solteira-SP
dc.description.affiliationUniversidade Federal de São Carlos (UFSCar), São Carlos-SP
dc.description.affiliationUnespUniversidade Estadual Paulista (UNESP), Ilha Solteira-SP
dc.format.extent595-597
dc.identifierhttp://www.feis.unesp.br/Home/departamentos/engenhariamecanica/maprotec/met_mat_abm2006.pdf
dc.identifier.citationMetalurgia e Materiais, v. 62, n. 572, p. 595-597, 2006.
dc.identifier.file2-s2.0-33845496558.pdf
dc.identifier.issn0104-0898
dc.identifier.lattes7193872294818689
dc.identifier.orcid0000-0002-5477-8139
dc.identifier.scopus2-s2.0-33845496558
dc.identifier.urihttp://hdl.handle.net/11449/69216
dc.language.isopor
dc.relation.ispartofMetalurgia e Materiais
dc.rights.accessRightsAcesso aberto
dc.sourceScopus
dc.subjectDislocation density
dc.subjectFerrite matrix
dc.subjectIntercritical annealing
dc.subjectWarm rolling
dc.subjectAnnealing
dc.subjectCarbon steel
dc.subjectDeformation
dc.subjectLaminating
dc.subjectMartensite
dc.subjectRolling
dc.subjectGrain size and shape
dc.titleGrãos ultrafinos por laminação a morno e recozimento intercríticopt
dc.title.alternativeUltrafine grains for lamination by warm rolling and intercritical annealingen
dc.typeArtigo
dspace.entity.typePublication
unesp.author.lattes7193872294818689
unesp.author.orcid0000-0002-5477-8139[1]
unesp.campusUniversidade Estadual Paulista (UNESP), Faculdade de Engenharia, Ilha Solteirapt
unesp.departmentEngenharia Mecânica - FEISpt

Arquivos

Pacote Original

Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
2-s2.0-33845496558.pdf
Tamanho:
1.59 MB
Formato:
Adobe Portable Document Format
Baixar

Coleções

Ilha Solteira - FEIS - Faculdade de Engenharia