dc.description.abstractEste trabalho investiga os efeitos de tratamento a plasma frio em polímeros convencionais, polipropileno e poliestireno, e em filme amorfo do tipo a-C-H, produzido através de Deposição Química de Vapor Assistida por Plasma (PECVD). Após etapas preliminares de escolha de gás e tempo a serem utilizados, as amostras foram tratadas em plasma de hexafluoreto de enxofre (SF6) em cinco diferentes potências e cinco diferentes pressões, totalizando 25 condições para cada substrato. As superfícies foram caracterizadas por goniometria, perfilometria, Espectroscopia de Infravermelho com Transformada de Fourier (FTIR), Microscopia Eletrônica de Varredura (MEV), Espectroscopia de Raios-X por Energia Dispersiva (EDS) e Espectroscopia de Fotoelétrons Excitados por Raios-X (XPS). Assim, foram examinados ângulo de contato, rugosidade, estrutura química, morfologia, composição química e composição química da superfície, respectivamente. O tratamento com SF6 aumenta a característica hidrofóbica dos três materiais, possivelmente devido à incorporação de flúor nas superfícies. A combinação de potência e pressão que promoveu aumento mais significativo em ϴ variou para cada material: 80 W e 80 mTorr para o filme amorfo, aumentando de 60,6° para 111,1° nestas condições, 20 W e 40 mTorr para o polipropileno, aumentando de 81,8° para 119° e 100 W e 60 mTorr para o poliestireno, aumentando de 74° para 95°. As análises por XPS indicaram a presença de flúor após os tratamentos com plasmas de SF6, mostrando um aumento da razão F/C de 0 para todas as amostras não tratadas para 0,03 para o filme amorfo tratado, 0,14 para o polipropileno tratado, e 0,60 para o poliestireno tratado.pt
dc.description.abstractThe present work investigates the effects of plasma treatment on conventional polymers, polypropylene and polystyrene, and on amorphous hydrogenated carbon, a-C-H, obtained by Plasma Enhanced Chemical Vapour Deposition, (PECVD). After preliminary studies to establish the plasma gas and treatment times, samples were treated in sulphur hexafluoride (SF6) plasmas at five different powers and five different pressures. Surfaces were characterized by goniometry, profilometry, Fourier Transform Infrared Spectrometry, Scanning Electron Microscopy (SEM), EnergyDispersive X-ray Spectroscopy (EDS) and X-Ray Photoelectron Spectroscopy (XPS). Thus, contact angle, roughness, chemical structure, morphology, chemical composition and surface chemical composition were examined. Results show that SF6 treatments increase the hydrophobicity of the three substrates, possibly due to the surface incorporation of fluorine. The power and pressure combinations that caused the greatest improvements in ϴ were as follows: 80 W and 80 mTorr for the amorphous film, resulting in an increase from 60.6° to 111.11°; 20 W and 40 mTorr for polypropylene, resulting in an increase from 81,8° to 119°; 100 W and 60 mTorr for polystyrene, resulting in an increase from 74° to 95°. The presence of fluorine following the SF6 plasma treatments was confirmed by the XPS analyses, which showed that F/C increased from 0 for all the untreated samples to 0,03 on treated amorphous films, to 0,14 on treated polypropylene, and to 0,60 on treated polystyrene.en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (UNESP)
dc.subjectTratamento a plasmapt
dc.subjectPolímerospt
dc.subjectFilmes finospt
dc.subjectHidrofóbicapt
dc.subjectPlasma treatmenten
dc.subjectPolymersen
dc.subjectThin filmsen
dc.subjectHydrophobicen
dc.titleTratamentos a plasma para a modificação de polímeros convencionais e polímeros depositados a plasmapt
dc.title.alternativePlasma treatments for surface modification of conventional polymers and plasma-deposited polymersen
dc.typeDissertação de mestrado
dc.contributor.institutionUniversidade Estadual Paulista (UNESP)
dc.rights.accessRightsAcesso aberto
unesp.graduateProgramCiência e Tecnologia de Materiais - FCpt
unesp.knowledgeAreaMateriaispt
unesp.researchArea"Não consta"pt
unesp.campusUniversidade Estadual Paulista (UNESP), Faculdade de Ciências, Baurupt
unesp.embargoOnlinept
dc.identifier.aleph000907631
dc.identifier.capes33004056083P7
Localize o texto completo

Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record