Influence of pack boriding on the wear and corrosion resistance of AISI H13 steel
Nenhuma Miniatura disponível
Data
2015-01-01
Autores
Heck, Stenio Cristaldo
Neto, Amadeu Lombardi
Picon, Carlos Alberto [UNESP]
Totten, George Edward
Casteletti, Luiz Carlos
Título da Revista
ISSN da Revista
Título de Volume
Editor
Resumo
In this work the effect of pack boriding time and temperature on the wear and corrosion resistance of AISI H13 tool steel was investigated. Steel samples were pack borided at 900 and 1000°C for periods of 2 and 4h; followed by non-abrasive fixed-ball microwear tests on borided and non-borided samples. The corrosion resistance was evaluated by potentiodynamic polarization tests in HCl 0.1M. High hardness layers were formed on the samples for all treatment conditions employed. The layer's properties, such as hardness, thickness, layer/substrate interface morphology and phases formed, were influenced by steel composition. For AISI H13 steel, which has a larger amount of alloying elements than carbon steel, the formed layers were harder, thinner, with a smoother interface. For all treatment conditions, the presence of Fe2B, FeB and CrB were identified. The wear and corrosion resistance of borided samples was significantly increased. The best results were obtained for samples borided at 1000°C.
Descrição
Palavras-chave
AISI H13, Boriding, Corrosion, Pack boriding, Wear
Como citar
European Conference on Heat Treatment 2015 and 22nd IFHTSE Congress - Heat Treatment and Surface Engineering from Tradition to Innovation.