Publicação: Mechanical Behavior of Ceramic Monolithic Systems With Different Thicknesses
Carregando...
Data
Orientador
Coorientador
Pós-graduação
Curso de graduação
Título da Revista
ISSN da Revista
Título de Volume
Editor
Operative Dentistry Inc
Tipo
Artigo
Direito de acesso
Acesso restrito
Resumo
Objectives: This study assessed the fully stabilized zirconia (FSZ) Prettau Anterior, the partially stabilized zirconia (PSZ) Prettau, and the lithium disilicate IPS e.max CAD (LD) through microstructural and mechanical characterization and effect of thickness on fracture load of the ceramics. Methods and Materials: Disk-shaped specimens (12 mm diameter and 1.2 mm thickness) were prepared for biaxial flexural strength (BFS) and Weibull statistics (n=30). For the fracture load static test (FLST) and Weibull statistics (n=30), disk-shaped specimens 12 mm in diameter and thicknesses of 0.5 mm, 1 mm, and 1.5 mm were cemented on an epoxy-resin substrate. Results: BFS (MPa) results were PSZ: 683.0 +/- 70.23; FSZ: 438.6 +/- 64.1; and LD: 248.6 +/- 37.3. One-way analysis of variance (ANOVA) for BFS was significant (p<0.001), and the Tukey post hoc test showed differences among all ceramics. There was difference in characteristic strength, but there was no difference in Weibull modulus. Two-way ANOVA for FLST was significant for ceramic (p<0001), thickness (p<0001), and interaction (p<0001). There was no difference among all ceramics at the 0.5 mm thickness. PSZ had higher values for the 1.0 mm and 1.5 mm thicknesses. LD of 1.5 mm thickness exhibited a higher FLST than FSZ. Conclusions: PSZ had the highest BFS, but when cemented on a substrate, all ceramics with 0.5 mm thickness behaved similarly. Despite the lower BFS, LD had a fracture load similar or superior to FSZ when cemented on a substrate.
Descrição
Palavras-chave
Idioma
Inglês
Como citar
Operative Dentistry. Indianapolis: Operative Dentistry Inc, v. 44, n. 5, p. E244-E253, 2019.