Effect of the surface treatment of plain carbon fiber posts on the retention of the composite core: an in vitro evaluation
Carregando...
Data
2001-03-01
Autores
Quintas, Adriana Ferreira [UNESP]
Bottino, Marco Antonio [UNESP]
Neisser, Maximiliano Piero [UNESP]
Araújo, Maria Auxiliadora Junho de [UNESP]
Título da Revista
ISSN da Revista
Título de Volume
Editor
Sociedade Brasileira de Pesquisa Odontológica e Faculdade de Odontologia da Universidade de São Paulo
Resumo
Foi avaliado o possível efeito de tratamentos superficiais em pinos de fibra de carbono lisos, quando comparados aos pinos serrilhados, na retenção à resina composta empregada na confecção de núcleos de preenchimento. Foram utilizados cinqüenta pinos de fibra de carbono, divididos em cinco grupos: os quatro primeiros grupos eram constituídos por pinos do tipo liso, cujas superfícies foram tratadas, e o último grupo por dez pinos do tipo serrilhado. Foram desenvolvidas matrizes de resina acrílica com um leito ajustado para conter o pino, com um alargamento na porção coronária para posterior preenchimento com resina composta. Após o tratamento superficial, todos os pinos receberam camadas de primer, foram secos e então ajustados à matriz de resina, colocando-se a resina composta autopolimerizável na porção coronária para um núcleo de preenchimento de 3 mm. As amostras foram submetidas a termociclagem e armazenadas em água destilada por uma semana. Os espécimes foram testados por meio de ensaios mecânicos de tração, à velocidade de 0,5 mm/min, até o deslocamento do conjunto ou a fratura da resina do núcleo. As conclusões foram as seguintes: a) o tratamento superficial nos grupos tratados por meio de jateamento (Grupo A), pontas diamantadas marcadoras de profundidade para facetas laminadas (Grupo C) e alteração da morfologia da extremidade coronária (Grupo D) conferiu aos pinos lisos valores de retenção comparáveis aos dos pinos serrilhados (Grupo E) nos ensaios de tração, porém sem diferença estatisticamente significativa entre estes grupos; b) os pinos tratados por meio de pontas diamantadas de granulação média (Grupo B) obtiveram valores de retenção menores que os demais grupos.
This study aims to evaluate the role of surface treatments performed on plain carbon fiber posts, in relation to serrated carbon fiber posts, in the retention of the composite core. Fifty carbon fiber posts received surface treatments in order to verify their influence on the retention of the core material. An acrylic resin mold was developed in order to precisely fit the post, leaving a machined space to accommodate a self-curing composite resin. After the surface treatment, a primer was applied on the coronal portion of all posts, which were then dried. They were fitted to the mold and received a 3 mm composite core. All specimens were thermocycled and then stored in distilled water for a week. Tension test was performed at a speed of 0.5 mm/min until there was lack of adhesion or fracture of the core. The conclusions were: a) the values of retention related to aluminum oxide spray (group A), depth cutter diamond burs (group C) and posts with machined coronal portion (group D) were comparable to those of serrated posts (group E), although no statistically significant difference between these groups was found; b) the mean values of core retention in group B (medium grit diamond burs) were statistically lower than those of other groups.
This study aims to evaluate the role of surface treatments performed on plain carbon fiber posts, in relation to serrated carbon fiber posts, in the retention of the composite core. Fifty carbon fiber posts received surface treatments in order to verify their influence on the retention of the core material. An acrylic resin mold was developed in order to precisely fit the post, leaving a machined space to accommodate a self-curing composite resin. After the surface treatment, a primer was applied on the coronal portion of all posts, which were then dried. They were fitted to the mold and received a 3 mm composite core. All specimens were thermocycled and then stored in distilled water for a week. Tension test was performed at a speed of 0.5 mm/min until there was lack of adhesion or fracture of the core. The conclusions were: a) the values of retention related to aluminum oxide spray (group A), depth cutter diamond burs (group C) and posts with machined coronal portion (group D) were comparable to those of serrated posts (group E), although no statistically significant difference between these groups was found; b) the mean values of core retention in group B (medium grit diamond burs) were statistically lower than those of other groups.
Descrição
Palavras-chave
Pinos dentários pré-fabricados, Resina composta, Retenção, Composite resins, Denture retention, Pre-fabricated post
Como citar
Pesquisa Odontológica Brasileira. Sociedade Brasileira de Pesquisa Odontológica e Faculdade de Odontologia da Universidade de São Paulo, v. 15, n. 1, p. 64-69, 2001.