Microdureza de resinas em função da cor e luz halógena
Carregando...
Data
2002-09-01
Autores
Martins, Fábio [UNESP]
Delbem, Alberto Carlos Botazzo [UNESP]
Santos, Luis Roque de Araújo dos [UNESP]
Soares, Hugo Leonardo de Oliveira [UNESP]
Martins, Eleonora de Oliveira Bandolin [UNESP]
Título da Revista
ISSN da Revista
Título de Volume
Editor
Sociedade Brasileira de Pesquisa Odontológica e Faculdade de Odontologia da Universidade de São Paulo
Resumo
O objetivo desse trabalho foi avaliar a influência da intensidade da luz e cor de uma resina composta no grau de dureza Knoop. Corpos-de-prova foram confeccionados utilizando-se matrizes de poliéster envoltas por um anel de cobre, contendo uma cavidade padronizada de 6 mm de diâmetro por 2 mm de espessura. Estas cavidades foram preenchidas com resina composta selecionada, Fill Magic - Vigodent, com as cores A3, B3, C3, D3 e I, fotopolimerizadas através de um fotopolimerizador Elipar, calibrado para produzir 3 intensidades de luz diferentes: 450 mW/cm², 800 mW/cm² e uma intensidade de luz crescente de 100 a 800 mW/cm². Foram confeccionados 90 corpos-de-prova em que o tempo de exposição da resina à luz halógena foi de 40 s. As amostras foram armazenadas em tubos de ensaio com água destilada a 37 ± 1ºC. Após este período, foram realizados os testes de dureza Knoop na região de superfície e fundo. Os resultados mostraram que houve diferença estatística em relação a intensidade de luz, entretanto em relação a cor, não houve diferença estatística. Os autores concluíram que a cor do compósito não influencia a dureza Knoop e que a intensidade progressiva promoveu os melhores resultados de dureza Knoop.
The aim of this study was to evaluate the influence of light intensity and the influence of the color of a composite resin on Knoop hardness. Samples were confected utilizing polyester matrices with 6 mm of diameter and 2 mm of depth. The matrices were filled with composite resin (Fill Magic - Vigodent), colors A3, B3, C3, D3 and I, and light-cured by means of an Elipar light-curing unit in three different light intensities: 450 mW/cm2, 800 mW/cm² and an increasing intensity setup of 100 mW/cm² to 800 mW/cm². Ninety test specimens were confected, with the standard curing time of 40 seconds. The specimens were stored at 37 ± 1ºC and immersed in distillate water. The Knoop test was carried out in superficial and deep areas of the specimens. The results revealed that there was no statistical difference (Tukey) between the tested colors. However, there was statistical difference between different light intensities. The authors concluded that the color of the composite resin did not influence Knoop hardness and that the progressive intensity setup led to the best Knoop hardness.
The aim of this study was to evaluate the influence of light intensity and the influence of the color of a composite resin on Knoop hardness. Samples were confected utilizing polyester matrices with 6 mm of diameter and 2 mm of depth. The matrices were filled with composite resin (Fill Magic - Vigodent), colors A3, B3, C3, D3 and I, and light-cured by means of an Elipar light-curing unit in three different light intensities: 450 mW/cm2, 800 mW/cm² and an increasing intensity setup of 100 mW/cm² to 800 mW/cm². Ninety test specimens were confected, with the standard curing time of 40 seconds. The specimens were stored at 37 ± 1ºC and immersed in distillate water. The Knoop test was carried out in superficial and deep areas of the specimens. The results revealed that there was no statistical difference (Tukey) between the tested colors. However, there was statistical difference between different light intensities. The authors concluded that the color of the composite resin did not influence Knoop hardness and that the progressive intensity setup led to the best Knoop hardness.
Descrição
Palavras-chave
Cimentos de resina, Dureza, Resinas compostas, Polímeros, Resin cements, Hardness, Composite resins, Polymers
Como citar
Pesquisa Odontológica Brasileira. Sociedade Brasileira de Pesquisa Odontológica e Faculdade de Odontologia da Universidade de São Paulo, v. 16, n. 3, p. 246-250, 2002.