Effect of silica coating on flexural strength of fiber posts
Nenhuma Miniatura disponível
Data
2006-01-01
Autores
Valandro, Luiz Felipe [UNESP]
Özcan, Mutlu
De Melo, Renata Marquez [UNESP]
Galhano, Graziela Avila Prado [UNESP]
Baldissara, Paolo
Scotti, Roberto
Bottino, Marco Antonio [UNESP]
Título da Revista
ISSN da Revista
Título de Volume
Editor
Resumo
Purpose: Fiber-reinforced composite (FRC) posts can be air-abraded to obtain good attachment to the resin cement. This study tested the effect of silica coating on the flexural strength of carbon, opaque, and translucent quartz FRC posts. Materials and Methods: Six experimental groups of FRC posts (n = 10 per group) were tested, either as received from the manufacturer or after chairside silica coating (30-μm CoJet-Sand). Results: There was no significant difference in the flexural strength of nonconditioned (504 to 525 MPa) and silica-coated (514 to 565 MPa) specimens (P > .05) (analysis of variance). The type of post did have a significant effect on flexural strength (P < .05). Conclusion: Chairside silica coating did not affect the flexural strength of both carbon and quartz FRC posts.
Descrição
Palavras-chave
biomedical and dental materials, epoxy resin, silicon dioxide, dental surgery, instrumentation, mechanical stress, scanning electron microscopy, surface property, tooth crown, tooth prosthesis, Air Abrasion, Dental, Coated Materials, Biocompatible, Dental Materials, Dental Prosthesis Design, Epoxy Resins, Microscopy, Electron, Scanning, Pliability, Post and Core Technique, Quartz, Silicon Dioxide, Stress, Mechanical, Surface Properties
Como citar
International Journal of Prosthodontics, v. 19, n. 1, p. 74-76, 2006.