Effect of molybdenum on the formation of Ti6Si2B in mechanically alloyed Ti-Mo-Si-B powders
Restricciones de acceso
MetadatosMostrar el registro completo del ítem
This paper discusses on effect of molybdenum on the Ti6Si2B formation in mechanically alloyed and hot-pressed Ti-xMo-22Si-11B (x= 2, 5, 7 and 10 at%) alloys. High-energy ball milling and hot pressing were utilized to produce homogeneous and dense materials, which were characterized by scanning electron microscopy, X-ray diffraction, electron dispersive spectrometry, and Vickers hardness. The excessive agglomeration during milling was more pronounced in Moricher powders, which was minimized with the formation of brittle phases. Hot pressing of mechanically alloyed Ti-xMo-22Si-11B powders produced dense samples containing lower pore amounts than 1%. Ti6Si2B was formed in microstructure of the hot-pressed Ti-2Mo-22Si-11B alloy only. In Mo-richer quaternary alloys, the Ti3Si and Ti5Si3 phases were preferentially formed during hot pressing. Oppositely to the ternary phase, the Ti3Si phase dissolved a significant Mo amount. Vickers hardness values were reduced in hot-pressed Ti-xMo-22Si-11B alloys containing larger Mo amounts, which were dissolved preferentially in Ti solid solution. © (2012) Trans Tech Publications, Switzerland.
Cómo citar este documento
Mostrando ítems relacionados por Título, autor o materia.
Influence of thermal and mechanical cycling on the flexural strength of ceramics with titanium or gold alloy frameworks Oyafuso, Denise Kanashiro ; Özcan, Mutlu; Bottino, Marco Antonio ; Itinoche, Marcos Koiti (Dental Materials, 2008) [Artigo]Objectives: The aim of this study was to evaluate the effect of thermal and mechanical cycling alone or in combination, on the flexural strength of ceramic and metallic frameworks cast in gold alloy or titanium. Methods: ...
Bindi, L.; Zaccarini, F.; Garuti, G.; Angeli, N. (Mineralogical Magazine, 2013) [Artigo]Chemical and structural data are reported for platinum-palladium intermediates from two nuggets found at Corrego Bom Sucesso, Minas Gerais, Brazil. Three grains with simple stoichiometries (i.e. PtxPd1 -x with x ∼0.67, ...
Souza, J. V C; Nono, M. C A; Mineiro, S. L.; Ribeiro, M. V. ; Silva, O. M M (Materials Science Forum, 2008) [Trabalho apresentado em evento]Due to their high hardness and wear resistance, Si3N4 based ceramics are one of the most suitable cutting tool materials for machining cast iron, nickel alloys and hardened steels. However, their high degree of brittleness ...