Fe K-edge X-ray absorption spectroscopy study of Pb(Fe2/3W 1/3)O3-PbTiO3 multiferroic ceramics
Data de publicação2013-03-21
Direito de acesso
MetadadosExibir registro completo
The present paper is a comprehensive study concerning Fe K-edge X-ray absorption spectroscopy (XAS) measurements, which were performed to characterize the local structure of (1 - x)Pb(Fe2/3W1/3)O 3-xPbTiO3 samples as a function of temperature and PbTiO3 content. Results obtained by the fits of extended X-ray absorption fine structure consist with rhombohedral symmetry for Pb(Fe 2/3W1/3)O3 composition at temperatures lower than room temperature. This result is in apparent disagreement with X-ray and neutron diffraction characterization which have been reported. This apparent disagreement is related to the fact that XAS probes the short-range order, whereas X-ray diffraction provides structural information about the average structure. Moreover, as the PbTiO3 content increases, a disorder has been detected at local structure of the FeO6 octahedron. Analysis of X-ray absorption near edge structure spectra did not show modifications in intensity nor energy of transitions. © 2013 American Institute of Physics.
Como citar este documento
Este item aparece nas seguintes coleções
Exibindo os itens relacionados pelo título, autor e palavra-chave.
Local electronic structure, optical bandgap and photoluminescence (PL) properties of Ba(Zr0.75Ti0.25)O3 powders Cavalcante, L. S. ; Batista, N. C.; Badapanda, T.; Costa, M. G S; Li, M. S.; Avansi, W.; Mastelaro, V. R.; Longo, Elson ; Espinosa, J. W M; Gurgel, M. F C (Materials Science in Semiconductor Processing, 2013) [Artigo]Ba(Zr0.75Ti0.25)O3 (BZT-75/25) powders were synthesized by the polymeric precursor method. Samples were structurally characterized by X-ray diffraction (XRD), Rietveld refinement, X-ray absorption near-edge structure (XANES) ...
Melo, D.; Vieira, F. T G; Costa, T. C C; Soledade, L. E B; Paskocimas, C. A.; Melo, D. M A; Longo, Elson ; Marinho, E. P.; Souza, A. G.; Santos, I. M G (Dyes and Pigments, 2013) [Artigo]In this work La1-xCaxCoO3 (x = 0-0.4) pigments were synthesized by the polymeric precursor method with heat treatments at 700, 800 and 900 C for 4 h. The powders were characterized by colorimetry, UV-vis spectroscopy and ...
Bashir, Abida; Ikram, M.; Kumar, Ravi; Lisboa Filho, Paulo Noronha ; Thakur, P. (Materials Science and Engineering B: Advanced Functional Solid-state Materials, 2010) [Artigo]We present the structural, electronic structure and magnetic studies of Ni doped SmFeO3. The X-ray diffraction (XRD) studies confirm the single phase nature of the samples having orthorhombic Pbnm structure and the unit-cell ...