Compressive strength of dental composites photo-activated with different light tips
Data de publicação2013-04-01
Direito de acesso
MetadadosExibir registro completo
The aim of this study was to evaluate the compressive strength of microhybrid (Filtek™ Z250) and nanofilled (Filtek™ Supreme XT) composite resins photo-activated with two different light guide tips, fiber optic and polymer, coupled with one LED. The power density was 653 mW cm -2 when using the fiber optic light tip and 596 mW cm-2 with the polymer. After storage in distilled water at 37 ± 2 °C for seven days, the samples were subjected to mechanical testing of compressive strength in an EMIC universal mechanical testing machine with a load cell of 5 kN and speed of 0.5 mm min-1. The statistical analysis was performed using ANOVA with a confidence interval of 95% and Tamhane's test. The results showed that the mean values of compressive strength were not influenced by the different light tips (p > 0.05). However, a statistical difference was observed (p < 0.001) between the microhybrid composite resin photo-activated with the fiber optic light tip and the nanofilled composite resin. Based on these results, it can be concluded that microhybrid composite resin photo-activated with the fiber optic light tip showed better results than nanofilled, regardless of the tip used, and the type of the light tip did not influence the compressive strength of either composite. Thus, the presented results suggest that both the fiber optic and polymer light guide tips provide adequate compressive strength to be used to make restorations. However, the fiber optic light tip associated with microhybrid composite resin may be an interesting option for restorations mainly in posterior teeth. © 2013 Astro Ltd.
Como citar este documento
Exibindo os itens relacionados pelo título, autor e palavra-chave.
Pinho, Sheila Zambello de ; Oliveira, José Brás Barreto de ; Gazola, Rodrigo José Cristiano ; Mazotti, Adriano César ; Molero, Camila Schimite ; Mendes, Carolina Borghi ; Mello, Denise Fernandes de ; Marques, Emilia de Mendonça Rosa ; Talamoni, Jandira Liria Biscalquini ; Silva, José Humberto Dias da et al. (Coleção PROGRAD (UNESP), 2011) [Livro]
Pinho, Sheila Zambello de ; Oliveira, José Brás Barreto de ; Pontes, Sueli Rodrigues ; Almeida, Djanira Soares de Oliveira e ; Godoy, Kathya Maria Ayres de ; Rosa, Claudia de Souza ; Nunes, Julianus Araújo ; Salvador, Sérgio Azevedo ; David, Célia Maria ; Vilche Peña, Angel Fidel et al. (Coleção PROGRAD (UNESP), 2011) [Livro]
Pinho, Sheila Zambello de ; Spazziani, Maria de Lourdes ; Mendonça, Sueli Guadelupe de Lima ; Rubo, Elisabete Aparecida Andrello ; Villarreal, Dalva Maria de Oliveira ; Duarte, Camila ; Okamoto, Mary Yoko ; Souza, Thais R. ; Garms, Gilza Maria Zauhy ; Marin, Fátima Aparecida Dias Gomes et al. (Coleção PROGRAD (UNESP), 2012) [Livro]