Intense photoluminescence emission at room temperature in calcium copper titanate powders
Restricciones de acceso
MetadatosMostrar el registro completo del ítem
A study was undertaken about the structural and photoluminescent properties at room temperature of CaCu3Ti4O12 (CCTO) powders synthesized by a soft chemical method and heat treated between 300 and 800 °C. The decomposition of precursor powder was followed by thermogravimetric analysis (TG-DTA), X-ray diffraction (XRD), Fourier transform infrared (FT-IR), Fourier transform Raman (FT-Raman) and photoluminescence (PL) measurements. XRD analyses revealed that the powders annealed at 800 °C are becoming ordered and crystallize in the cubic structure. The most intense PL emission was obtained for the sample calcined at 700 °C, which is not highly disordered (300-500 °C) and neither completely ordered (800 °C). From the spectrum it is clearly visible that the lowest wavelength peak is placed around 480 nm and the highest wavelength peak at about 590 nm. The UV/vis absorption spectroscopy measurements showed the presence of intermediate energy levels in the band gap of structurally disordered powders. © 2012 Elsevier Ltd and Techna Group S.r.l.
Cómo citar este documento
Mostrando ítems relacionados por Título, autor o materia.
Local electronic structure, optical bandgap and photoluminescence (PL) properties of Ba(Zr0.75Ti0.25)O3 powders Cavalcante, L. S. ; Batista, N. C.; Badapanda, T.; Costa, M. G S; Li, M. S.; Avansi, W.; Mastelaro, V. R.; Longo, Elson ; Espinosa, J. W M; Gurgel, M. F C (Materials Science in Semiconductor Processing, 2013) [Artigo]Ba(Zr0.75Ti0.25)O3 (BZT-75/25) powders were synthesized by the polymeric precursor method. Samples were structurally characterized by X-ray diffraction (XRD), Rietveld refinement, X-ray absorption near-edge structure (XANES) ...
Xavier, C. S.; De Moura, A. P. ; Li, M. S.; Varela, José Arana ; Longo, Elson ; Cava, S. (Technical Proceedings of the 2012 NSTI Nanotechnology Conference and Expo, NSTI-Nanotech 2012, 2012) [Trabalho apresentado em evento]In this work, zinc oxide powders were synthesized by microwave-assisted hydrothermal method in basic medium. These powders were analyzed by X-ray diffraction (XRD), Field-emisson gum scanning electron microscopy (FEG-SEM), ...
Photoluminescence property of Ba(Zr0.25Ti0.75)O-3 powders prepared by solid state reaction and polymeric precursor method Rout, S. K.; Cavalcante, L. S. ; Sczancoski, J. C. ; Badapanda, T.; Panigrahi, S.; Li, M. Siu; Longo, Elson (Physica B: Condensed Matter, 2009) [Artigo]Ba(Zr0.25Ti0.75)O-3 (BZT) powders were synthesized by the polymeric precursor method (PPM) at different temperatures (400, 500 and 700 degrees C) for 2 h and by the solid state reaction (SSR) at 1350 degrees C for 4 h. ...