dc.identifier.citationCÁCERES BENÍTEZ, Pablino. Influência da temperatura sobre a microdureza de uma resina composta fotoativada com luz halógena e Leds. 2004. 101 f. Dissertação (mestrado) - Universidade Estadual Paulista, Faculdade de Odontologia de Araraquara, 2004.
dc.identifier.urihttp://hdl.handle.net/11449/89631
dc.description.abstractO objetivo desta pesquisa foi avaliar a influência de várias temperaturas sobre os valores de microdureza de topo e base de uma resina composta fotopolimerizável comercialmente disponível, variando o tipo de fonte de luz (LEDs e lâmpada halógena). As temperaturas testadas foram 25, 35, 45, 55, 65, 80, 90 e 100º C. A resina composta utilizada foi a Z100 (3M). Com o auxílio de uma matriz metálica foram confeccionados 3 corpos-de-prova de 2 mm de espessura e 9,8 mm de diâmetro para cada temperatura. Os corpos-de-prova foram polimerizadas LEDs (60 s) ou lâmpada halógena (40 s) enquanto eram submetidas às diferentes temperaturas, após a polimerização as amostras foram armazenadas a seco, em estufa a 37º C. Após 24 horas as amostras foram submetidas ao teste de microdureza Vickers no topo e na base. Baseados nos resultados conclui-se que com a elevação da temperatura aumentou o valor da dureza Vickers com correlação linear positiva e com ambos aparelhos; o valor da dureza de topo foi sempre superior à dureza de base independentemente da fonte de luz ou temperaturas empregadas; o aparelho de luz halógena só se mostrou superior à fonte de LEDs na região de base dos corpos-de-prova.pt
dc.description.abstractThe aim of this research was to evaluate the influence of several temperatures on the microhardness values of top and base of a light curing composites resin commercially available, varying the type of light source (LEDs and halogen lamp). The tested temperatures were 25, 35, 45, 55, 65, 80, 90 and 100º C. The composite resin used was Z100 (3M). With the aid of a metallic mould were made three samples of 2 mm of thickness and 9,8 m diameter for each temperature. The samples were light cure while they where submitted to the different temperatures with LEDs (60 s) and halogen lamp (40 s), after the polymerization the samples were dry stored in a stove at 37º C. After 24 hours, the samples were submitted to the Vickers microhardness test in the top and in the base. Based on the results it was concluded that with the elevation of the temperature increased the Vickers hardness value with positive linear correlation on both devices. The hardness value of the top was always superior to the base hardness, independently of the light source or used temperatures. The halogen lamp source was superior to the source of LEDs in the area of base of the samples.en
dc.description.sponsorshipConselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
dc.format.extent101 f. : il.color.
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (UNESP)
dc.sourceAleph
dc.subjectResinas compostaspt
dc.subjectTestes de durezapt
dc.subjectCalorpt
dc.subjectAparelhos fotopolimerizadorespt
dc.subjectComposite resinsen
dc.subjectHardness testen
dc.subjectHeaten
dc.subjectCuring light sourcesen
dc.titleInfluência da temperatura sobre a microdureza de uma resina composta fotoativada com luz halógena e Ledspt
dc.typeDissertação de mestrado
dc.contributor.institutionUniversidade Estadual Paulista (UNESP)
dc.rights.accessRightsAcesso aberto
unesp.graduateProgramCiências Odontológicas - FOARpt
unesp.knowledgeAreaDentística restauradorapt
unesp.campusUniversidade Estadual Paulista (UNESP), Faculdade de Odontologia, Araraquarapt
dc.identifier.aleph000284558
dc.identifier.filecaceresbenitez_p_me_arafo.pdf
dc.identifier.capes33004030010P2
Localize o texto completo

Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record