Effect of oxidizing atmosphere on the electrical properties of SrBi4Ti4O15 thin films obtained by the polymeric precursor method
(Solid State Sciences, 2008-12-01) [Artigo]
Strontium bismuth titanate (SrBi4Ti4O15) thin films were deposited on (111) Pt/Ti/SiO2/Si Substrates by spin coating from the polymeric precursor method. Annealing in static air and dynamic oxygen atmosphere was performed ...
Dielectric properties of soft chemical method derived CaCu3Ti4O12 thin films onto Pt/TiO2/Si(100) substrates
(Journal of Alloys and Compounds, 2011-03-03) [Artigo]
Calcium copper titanate, CaCu3Ti4O12 (CCTO), thin film has been deposited by the soft chemical method on Pt/Ti/SiO2/Si (1 0 0) substrates at 700 degrees C for 2 h. The peaks were indexed as cubic phase belonging to the ...
Fatigue and retention properties of Bi3.25La0.75Ti3O12 films using LaNiO3 bottom electrodes
(Materials Characterization, 2009-05-01) [Artigo]
Fatigue-free Bi3.25La0.75Ti3O12 (BLT) thin films were grown on LaNiO3 bottom electrodes grown in a microwave furnace at 700 degrees C for 10 min from the polymeric precursor method. It was found that LaNiO3 (LNO) bottom ...
Retention characteristics of lanthanum-doped bismuth titanate films annealed at different furnaces
(Materials Chemistry and Physics, 2009-05-15) [Artigo]
Lanthanum-doped bismuth titanate thin films (Bi(3.25)La(0.75)Ti(3)O(12) - BLT) were prepared by the polymeric precursor method and crystallized in the microwave and conventional furnaces. The obtained films are polycrystalline ...