dc.contributor.advisorChinaglia, Dante Luis [UNESP]
dc.contributor.authorStefanelo, Josiani Cristina [UNESP]
dc.date.accessioned2014-06-11T19:25:31Z
dc.date.available2014-06-11T19:25:31Z
dc.date.issued2009-10-05
dc.identifier.citationSTEFANELO, Josiani Cristina. Estudo das propriedades elétro-óptica de dispositivos eletroluminescentes confeccionados com um compósito híbrido. 2009. 77 f. Dissertação (mestrado) - Universidade Estadual Paulista, Instituto de Geociências e Ciências Exatas, 2009.
dc.identifier.urihttp://hdl.handle.net/11449/91900
dc.description.abstractNeste trabalho foi desenvolvido um dispositivo eletroluminescente (EL) constituído de um compósito híbrido (CH), formado por uma blenda polimérica e um material EL inorgânico. A blenda é composta por um polímero condutor, a poli(o-metoxianilina) (POMA) dopada com ácido tolueno sulfônico (TSA), e um polímero isolante, o poli(fluoreto de vinilideno-co-trifluoretileno) (P(VDF-TrFE)). A esta blenda é acrescentado um material EL inorgânico, o silicato de zinco dopado com Manganês (Zn2SiO4:Mn), formando assim, o compósito híbrido. O dispositivo foi construído depositando o compósito por drop casting sobre um substrato de óxido de estanho dopado com flúor (FTO) e após cristalização em uma estufa foi depositado um eletrodo de metal por evaporação à vácuo formando uma estrutura tipo “sanduíche”. Neste trabalho foram construídos dispositivos com eletrodo superior de Alumínio (Al) e Ouro (Au), denominados: FTO/CH/Al e FTO/CH/Au. O comportamento elétrico dos dispositivos de FTO/CH/Al foram analisados aplicando-se as teorias de Emissão Termoiônica, Emissão Schottky e Emissão Poole-Frenkel, o que tornou possível encontrar alguns parâmetros como: altura da barreira para a junção metal/CH, condutividade do CH e fator de retificação. O dispositivo de FTO/CH/Au foi caracterizado pela técnica de espectroscopia de impedância, sendo obtido também a altura da barreira para a junção metal/CH, a condutividade do CH, além da constante dielétrica do compósito e como variam esses dois últimos parâmetros com a temperatura. A aplicação das teorias de Emissão Termoiônica, Emissão Schottky e Emissão Poole-Frenkel produziram resultados semelhantes aos obtidos pela técnica de espectroscopia de impedância. Os espectros de luminescência apresentaram um pico em l = 528 nm com estabilidade temporal de emissão comparável a dos dispositivos inorgânicos puros.pt
dc.description.abstractIn this work was developed an electroluminescent (EL) device made up with a hybrid composite (CH), that is formed by a polymeric blend and an inorganic EL material. The conductive polymer, poly(o-methoxyaniline) (POMA) doped with p-Toluene sulphonic acid (TSA), and an isolating polymer, the poly(vinylidenefluoride-co-trifluoroethylene) (P(VDFTrFE)), was used to make the polymer blend. An inorganic EL material, the zinc silicate manganese-doped (Zn2SiO4:Mn), was added to the blend, forming the hybrid composite. The composite was deposited by drop-casting over a Fluoride Tin Oxide substrate (FTO) and after the crystallization in an oven a metal electrode was deposited by vacuum evaporation, forming a type “sandwich” structure. In this work were constructed different devices. Aluminum (Al) and Gold (Au) were used as upper electrodes, therefore the device structures were: FTO/CH/Al and FTO/CH/Au. To analyze the electrical behavior of the FTO/CH/Al device was applied the theories of Thermionic Emission, Schottky Emission and Poole- Frenkel Emission. Using these theories was possible to obtain parameters such as; the barrier height from the metal/CH junction, CH conductivity and diode rectifier factor. The FTO/CH/Au device was characterized using the impedance spectroscopy technique. For this device was also possible to obtain the barrier height from the metal/CH junction, CH conductivity and CH dielectric constant. For the last two parameters the dependence with the temperature were also observed. The application of the theories of Thermionic Emission, Schottky Emission and Poole-Frenkel Emission produced similar results to that obtained by the impedance spectroscopy technique. The luminescence spectra, for the devices, showed a peak at l = 528 nm with emission stability in time that it is comparable of pure inorganic devices.en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.format.extent77 f. : il., tabs.
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (UNESP)
dc.sourceAleph
dc.subjectPolimerospt
dc.subjectEspectroscopia de impedanciapt
dc.subjectCompósito (POMA/P(VDF-TrFE/Zn2SiO4:Mn)pt
dc.subjectDispositivo emissor de luzpt
dc.subjectEmissão termoiônicapt
dc.subjectEmissão Schottkypt
dc.subjectEmissão Poole-Frenkelpt
dc.subjectLight emitting deviceen
dc.subjectThermionic emission and schottky emissionen
dc.subjectImpedance Spectroscopyen
dc.subjectPoole-frenkel emissionen
dc.titleEstudo das propriedades elétro-óptica de dispositivos eletroluminescentes confeccionados com um compósito híbridopt
dc.typeDissertação de mestrado
dc.contributor.institutionUniversidade Estadual Paulista (UNESP)
dc.rights.accessRightsAcesso aberto
unesp.graduateProgramFísica - IGCEpt
unesp.knowledgeAreaFísica aplicadapt
unesp.campusUniversidade Estadual Paulista (UNESP), Instituto de Geociências e Ciências Exatas, Rio Claropt
dc.identifier.aleph000602142
dc.identifier.filestefanelo_jc_me_rcla.pdf
dc.identifier.capes33004137063P6
dc.identifier.lattes8870539749821067
unesp.author.lattes8870539749821067
Localize o texto completo

Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record