dc.identifier.citationNOGUEIRA, Rosiane de Castro. Estudo do efeito do tempo e do meio de moagem de alta energia para obtenção de pós nanométricos de hidretos de titânio e nióbio. 2009. 106 f. Dissertação (mestrado) - Universidade Estadual Paulista, Faculdade de Engenharia de Guaratinguetá, 2009.
dc.identifier.urihttp://hdl.handle.net/11449/94419
dc.description.abstractAs ligas Ti-Nb são apropriadas para uso em implantes devido a sua alta resistência e biocompatibilidade. Um dos métodos de obter estas ligas é a metalurgia do pó, pois ele permite obter peças próximas ao seu formato final. Teorias indicam que a razão de densificação varia inversamente como uma função do tamanho da partícula. O aumento de interesse na fabricação de materiais nanoestruturados (partículas menores que 100 nm) é devido à possibilidade de obter um material sinterizado em um tempo menor e em temperaturas mais baixas, com uma melhor densificação do que pós convencionais, pois é mais reativo. Neste trabalho, após hidrogenação e moagem de alta energia por até 60 min, obteve-se pós de hidreto de titânio e hidreto de nióbio, com estrutura ultrafina/nanométrica, que auxilia o processo de difusão numa posterior etapa de sinterização. Meios de moagem de diferentes materiais (aço inoxidável e nitreto de silício - Si3N4) foram usados. Independentemente dos meios de moagem usados, o material obtido apresentou aproximadamente 5% das partículas com valores cumulativos de tamanhos de até 100 nm. Mas, o material obtido do recipiente de Si3N4 após 20 min de moagem apresentou uma maior porcentagem de partículas com diâmetros médios equivalentes entre 40 nm e 1000 nm, correspondente a 29%.pt
dc.description.abstractThe Ti-Nb alloys are suitable for use in implants due to their high tensile strength and biocompatibility. One of the methods to obtain these alloys is the powder metallurgy, because it allowing to get pieces closer to near-net-shape. Theories showing that the densification rate range conversely like a function of the grain size. The great interest in the manufacturing of nanostructured materials – NsM (particles smaller than 100 nm) is due to possibility to obtain a sintered material in a smaller time and in more low temperatures than conventional powders, with the best densification, because it is more reactive. In this work, after hydrogenation and use of higher energy ball milling by until 60 min, were obtained powders of titanium hydride and niobium hydride, with ultra-fine/nanometric structure, what help in the diffusion process during a later stage of sintered. Milling medium of different materials (stainless steel and silicon nitride - Si3N4) were used. Independently of the grinding medium used, the material obtained exhibit approximating 5% of the particles with the cumulative values of size until 100 nm. But, is the possible to verify that the material obtained of the Si3N4 vessel, after milling by 20 min, exhibited a greater percentage of particles with average equivalent diameters between 40 nm and 1000 nm, than correspond to 29%.en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
dc.format.extent106 f. : il.
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (UNESP)
dc.sourceAleph
dc.subjectMetalurgia do popt
dc.subjectLigas de titaniopt
dc.subjectNiobiopt
dc.subjectPowder metallurgyen
dc.subjectTi-Nb alloysen
dc.subjectMicrostructureen
dc.titleEstudo do efeito do tempo e do meio de moagem de alta energia para obtenção de pós nanométricos de hidretos de titânio e nióbiopt
dc.typeDissertação de mestrado
dc.contributor.institutionUniversidade Estadual Paulista (UNESP)
dc.rights.accessRightsAcesso aberto
unesp.graduateProgramEngenharia Mecânica - FEGpt
unesp.knowledgeAreaMateriaispt
unesp.campusUniversidade Estadual Paulista (UNESP), Faculdade de Engenharia, Guaratinguetápt
dc.identifier.aleph000602648
dc.identifier.filenogueira_rc_me_guara.pdf
dc.identifier.capes33004080027P6
dc.identifier.lattes1868573083430307
unesp.author.lattes1868573083430307
Localize o texto completo

Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record