The use of thermogravimetric analysis to characterize the metallic slag aggregates in structural concrete

Nenhuma Miniatura disponível




de Medeiros, Tiziana Azario
Fischer, Eliane Kujat
Amoresi, Rafael Aparecido Ciola [UNESP]
Zaghete, Maria Aparecida [UNESP]
Stropa, Jusinei Meireles
de Oliveira, Lincoln Carlos Silva
Cavalheiro, Alberto Adriano

Título da Revista

ISSN da Revista

Título de Volume



Structural concretes must have a set of chemical characteristics to present a satisfactory resistance to the degradation in environment conditions. Besides the several types of mineralogical compositions, the calcium-rich sulfates, silicates and aluminates phases appear as majority components, but the gypsum one seems to play the most important rule in morphological changes during the concrete cure. In this work, it was carried out several characterizations in commercial Portland cement and the structural concrete sample. Nitrogen adsorption isotherms at 77 K for Portland cement showed the thermal treatment at 500 ºC does not undergo significant decreasing in surface area due the high content of porous silicates and aluminates components. The additional resistance to the corrosion of structural concretes exposed at environment conditions can be associated to presence of slag metallic aggregates, which could be characterized successfully by thermal analysis. The amount of embedded metallic component in concrete sample was detected by typical weight gain originated form oxygen incorporation above 700 ºC.



Portland cement, Slag metallic aggregate, Structural concrete

Como citar

Materials Science Forum, v. 1012 MSF, p. 272-277.