Endodontics Braz Oral Res 2008;22(1):25-30 25 The effect of endodontic materials on the optical density of dyes used in marginal leakage studies Abstract: The aim of this study was to determine the effect of the ex- posure of different endodontic materials to different dye solutions by evaluating the optical density of the dye solutions. Seventy-five plastic tubes were filled with one of the following materials: AH Plus, Seala- pex, Portland cement, MTA (Angelus and Pro Root) and fifteen control plastic tubes were not. Each specimen of material and control was im- mersed in a container with 1 ml of each dye solution. A 0.1 ml-dye solu- tion aliquote was removed before immersion and after 12, 24, 48 and 72 hours of each specimen immersion to record its optical density (OD) in a spectrophotometer. Statistical analysis was performed with ANOVA and Tukey tests (5%). No significant difference was found among any of the solution OD values for AH Plus cement. Portland cement promoted different OD values after 12 hours of immersion. MTA-Angelus cement presented different OD values only for 2% rhodamine B and the MTA- Pro Root cement presented different OD values in all 2% rhodamine B samples. Sealapex cement promoted a reduction in the India Ink OD val- ues. Dye evaluation through OD seems to be an interesting method to select the best dye solution to use in a given marginal leakage study. Descriptors: Dental leakage; Methylene blue; Spectrophotometry; Methods. Claudio Hideki Kubo(a) Marcia Carneiro Valera(a) Ana Paula Martins Gomes(a) Maria Nadir Gasparoto Mancini(b) Carlos Henrique Ribeiro Camargo(a) (a)PhDs in Endodontics, Department of Restorative Dentistry; (b)PhD in Biochemistry – School of Dentistry of São José dos Campos, São Paulo State University (UNESP). Endodontics Corresponding author: Claudio Hideki Kubo Rua Guaripé, 95, Casa 1, Saúde São Paulo - SP - Brazil CEP: 04147-070 E-mail: chkubo1@ig.com.br Received for publication on Mar 26, 2007 Accepted for publication on May 29, 2007 The effect of endodontic materials on the optical density of dyes used in marginal leakage studies Braz Oral Res 2008;22(1):25-3026 Introduction Many dyes in different concentrations have been used in leakage studies, such as 5% eosin,1 India ink,1,2 silver nitrate,3-5 methylene blue1,5-8 and rhoda- mine B.5,8-10 However, dyes can chemically interact with sealing materials or dentin, which may influ- ence its diffusion or promote tracer decoloration, impairing an adequate marginal leakage evalua- tion.7,11-13 The purpose of the present study was to determine the different material exposure effects on a 2% methylene blue solution in phosphate buffer at pH 7 (MB), on blue India ink in phosphate buffer at pH 7 (BII), and on a 2% rhodamine B solution in phosphate buffer at pH 7 (RB) after different im- mersion periods using optical density (OD). Material and Methods A methylene blue solution in phosphate buffer at pH 7 (MB) was prepared using 2 g of methylene blue (Synth, Labsynth Produtos para Laboratórios Ltda., Diadema, SP, Brazil) in 100 ml of 0.2 M phosphate buffer at pH 7.0. Blue India ink (BII) (Quink, Parker Pen Holding Ltd., Epping, England, pHinitial= 2.47) was buffered by addition of 5.4 g of sodium phos- phate dibasic (Na2HPO4.7H2O, Reagentes Ecibra, Equipamentos científicos do Brasil, São Paulo, SP, Brazil) and 2.78 g of sodium phosphate monobasic (NaH2PO4.7H2O, Reagentes Ecibra, Equipamentos científicos do Brasil, São Paulo, SP, Brazil) in 100 ml of India ink. After total salt dissolution, pH was ad- justed to 7 with sodium phosphate dibasic, 2 M so- lution drops. Two percent rhodamine B solution in phosphate buffer at pH 7 (RB) was prepared dissolv- ing 2 g of rhodamine B dye (Synth, Labsynth Produ- tos para Laboratórios Ltda., Diadema, SP, Brazil) in 100 ml of 0.2 M phosphate buffer at pH 7. The wavelength at maximum absorption of the dyes was determined with the scan spectrum rang- ing from 100 to 1,000 nm in a Shimadzu spectro- photometer (Model UV1203, Kyoto, Japan). The methylene blue solution presented maximum ab- sorption at 596 nm, the blue India ink, at 585 nm, and the rhodamine B dye solution, at 566 nm. Ninety 1 mm-thick wall, 2 mm-inner diameter and 10 mm-long standardized plastic tubes (Embramed equipo, Embramed Ind. Com. Ltda., São Paulo, SP, Brazil) were prepared. Plastic tubes were used be- cause they allow the production of specimens with standardized shape and size according to the pilot study, and serve as a matrix for the different dental filling materials. The materials tested were AH Plus endodontic cement (Dentsply De Trey GMbH, D- 78467 Konstanz, Germany), Sealapex (Kerr Corp., subsidiary of Sybron, Orange, CA, USA), Portland cement (CPII type, Votorantim, Votorantim, São Paulo, Brazil), MTA-Angelus (Odonto-Lógika, Londrina, PR, Brazil) and Pro Root-MTA endodon- tic cements (Denstply, Tulsa Dental, Tulsa, OK, USA). The materials were manipulated according to the manufacturers’ recommendations and the tubes were filled using a lentulo size 4 (Maillefer S.A., Ballaigues, Switzerland) mounted on a contra-angle handpiece (KaVo do Brasil S.A., Joinville, SC, Bra- zil) running at moderate speed. Fifteen specimens were obtained per material. Specimens were kept in 100% humidity at 37 C for 24 hours to allow the materials to set before dye immersion.7 Fifteen plastic tubes were not filled by any test material and served as the control group. Five specimens of each material were immersed individually in the MB, BII and RB solutions. Each specimen was immersed in 1 ml of the dye solution and stored in an amber glass container. 0.1 ml-aliquots of sample dyes were removed from the glass containers, put in a test tube, diluted in 1.9 ml of deionized water. Optical densities were registered in a Shimadzu spectrophotometer (Model UV - 1203, Kyoto, Japan) at 596, 585 and 566 nm for methylene blue, India ink and rhodamine B, re- spectively. Optical densities (OD) were registered before (t0) and after 12, 24, 48 and 72 immersion hours of each material. Absorbance data were sub- mitted to the three-way ANOVA and the Tukey multiple comparison test was used. Both statisti- cal analyses were performed at the 5% significance level. Results Graph 1 shows the OD means for each dye be- fore and after each immersion period for each mate- rial analyzed. The ANOVA test showed significant variability among all factors analyzed (p = 0.00). Kubo CH, Valera MC, Gomes APM, Mancini MNG, Camargo CHR Braz Oral Res 2008;22(1):25-30 27 2% methylene blue aqueous solution in phosphate buffer at pH 7 (MB) In relation to t0, it was observed that the control group did not show significant changes (p > 0.05) for OD at any analysis interval. AH Plus and Port- land cements decreased OD values. MTA-Angelus, MTA-Pro Root and Sealapex increased OD in rela- tion to t0. However, only in the Sealapex group these differences were significant (p > 0.05) (Graph 1). India ink in phosphate buffer at pH 7 (BII) There was a tendency for decreased OD values in control specimens, and in the AH Plus cement, Port- land cement, MTA-Angelus and Sealapex groups. However, these differences were significant only in control specimens (p < 0.05), and in those of the Portland cement (p < 0.05), and Sealapex groups after 48 hours (p = 0.00) and 72 hours (p = 0.00) (Graph 1). Aqueous solution of 2% rhodamine B in phosphate buffer at pH 7 (RB) In relation to t0, immersion of specimens in the control and AH Plus cement groups presented ten- dency to decrease dye OD values. However, the difference was significant (p = 0.03) only for the 12-hour period of AH Plus cement. For the MTA- Angelus, MTA-Pro Root and Sealapex groups, there was significant OD increase in all time periods (p < 0.05) (Graph 1). Material effect on dye OD The optical density observed after immersion of the control group in BII (pH 7) and in RB (pH 7) was statistically the same (p > 0.05) for each period analyzed (12, 24, 48 and 72 hours) and was statisti- cally different when compared to that observed after immersion in MB (pH 7) (Graph 1). The OD values for all dye solutions after AH Plus cement immersion were statistically similar. A significant OD reduction was observed only for the first 12 hours (Graph 1). The OD values observed after Portland cement group immersion in MB or RB were statistically the same for each period analyzed. However, for BII the OD values were statistically different (p < 0.05) after 24, 48 and 72 hours (Graph 1). In the MTA- Angelus and MTA-Pro Root cement groups, RB OD values were statistically higher than those observed with MB after 48 and 72 hours of immersion and higher than those observed with BII after 12, 24, 48 and 72 hours (Graph 1). In the Sealapex cement group, no statistical differences were observed in OD values after immersion in MB or RB. However, higher significant differences for OD values of MB Plot of optical density means Hours Control O pt ic al D en si ty 0.4 0.5 0.6 0.7 0.8 0.9 1.0 1.1 1.2 1.3 0 12 24 48 72 Hours AH Plus 0 12 24 48 72 Hours Portland 0 12 24 48 72 Hours Angelus 0 12 24 48 72 Hours Pro Root 0 12 24 48 72 Hours Sealapex 0 12 24 48 72 Methylene blue India Ink Rhodamine B Graph 1 - Optical density means observed for each dye in each period analyzed, grouped by material sample. The effect of endodontic materials on the optical density of dyes used in marginal leakage studies Braz Oral Res 2008;22(1):25-3028 and RB were observed when compared to those ob- served with BII for each period analyzed. Discussion Methylene blue is susceptible to oxidation and amino groups are readily hydrolyzed to thional (col- orless compound – pH > 7), or can decolorize when in contact with zinc or sulfuric acid solutions.13-15 According to Starkey et al.16 (1993) and Wu, Wes- selink11 (1993), specimen immersion in different so- lutions of MB with pH 5, for different periods can demineralize the dentin and allow dye penetration. Phosphate buffer was chosen because it allowed the use of these solutions at pH = 7 and because it pre- vents pH variation.17 Wu et al.13 (1998) and Oztan et al.7 (2001) ana- lyzed dye stability before and after contact with a variety of dental materials. In their study, five speci- mens were filled with materials in plastic tubes and were exposed to 0.8 ml of a given dye in one of its extremities to simulate a marginal leakage by dye experiment. In this study, a specimen filled with each material in a plastic tube was immersed in a 1 ml-container filled with one of the three dye so- lutions evaluated, which allowed material contact with dye in both extremities. Wu et al.13 (1998) also used a 596 nm wavelength to determine changes in OD for methylene blue so- lution at pH 7. However, Oztan et al.7 (2001) did not take into consideration the type of dye and used a 416 nm wavelength to determine the dye change at optical density. OD dye analysis at t0 was performed before material immersion, following the same Wu et al.13 (1998) protocol. However, the difference in methodology, use of buffer and concentration of the methylene blue solution may have contributed to the difference in control group OD values at t0 in the present study (ODMB 2% = 0.764 0.039) compar- ing to the results found by Wu et al.13 (1998) (ODMB 1% = 0.639 0.002). Oztan et al.7 (2001) observed different OD values among different experimental groups at t0 because evaluation was performed immediately after materi- al immersion in dye. The dye solution buffering and the wavelength difference ( = 416 nm) used by Oz- tan et al.7 (2001) to evaluate dye solution OD could have contributed for the different control group/MB OD values at t0. In the present study, the India ink evaluated was blue while Oztan et al.7 (2001) used black India ink. The color of the India ink, the buff- ering, and methodology differences could have con- tributed to the different OD values observed for the control group in the present study at t0. In the present study, the AH Plus cement group promoted continuous OD reduction of all dye solu- tions used. Oztan et al.7 (2001) observed continu- ous OD increase when AH Plus cement specimens were immersed in 2% methylene blue solution at pH 7. The 2% methylene blue solution buffering in the present study could have avoided the interaction between the dye solution and the AH Plus cement chemical compounds, thus avoiding cement struc- ture particles transference to the solution. Estrela et al.18 (2000) observed that MTA and two brands of Portland cement contained the same chemical components, except for the bismuth present in MTA. In the present study, there was no statistical difference between MTA-Angelus and MTA-Pro Root specimens immersed in the same solution and for the same period of time (Graph 1). MTA-Angelus and MTA-Pro Root are brand names for mineral triox- ide aggregate, which, according to Wu et al.13 (1998), can decolorize the methylene blue solution when used in marginal leakage studies. MTA has calcium ox- ide in its composition and, when it reacts with wa- ter, it forms calcium hydroxide which dissociates and increases the pH environment, promoting solution decolorizing.7,13,19,20 However, differently from Wu et al.13 (1998), in the present study the dye solutions were prepared with phosphate buffer at pH 7, and when 2% MB aqueous solution (pH 7) and BII (pH 7) were evaluated, no OD value reduction was seen after MTA immersion (both Angelus and Pro Root). Simi- lar results were observed when Portland cement speci- mens were immersed in 2% MB aqueous solution and in RB for 24, 48 and 72 hours (Graph 1). Kubo et al.9 (2005) evaluated the seal of root apexes retrofilled with Pro Root for marginal leak- age with RB aqueous solution (pH 7) and dye pen- etrated 1.89 mm. In previous studies,6,8,21 it was ob- served that the dye solution penetrated from 0.28 to 0.31 mm. For Oztan et al.7 (2001), the OD means Kubo CH, Valera MC, Gomes APM, Mancini MNG, Camargo CHR Braz Oral Res 2008;22(1):25-30 29 increase caused by transfer of soluble particles of the material tested to the dye solution interferes in dye penetration evaluation in marginal leakage studies. In the present study, a bigger RB interaction with MTA-Angelus specimens and MTA-Pro Root speci- mens was observed, thus promoting a significant OD increase after t0. On the other hand, a small OD decrease is better than its increase because a small OD reduction indicates dye soluble particle trans- fer to the material tested, which does not interfere in marginal leakage studies.7 However, an OD de- crease can also be caused by material soluble par- ticle interaction with the dye solution by formation of a colorless chemical solution.13 The Portland cement group presented OD reduc- tion and the lowest OD values after 24, 48 and 72 immersion hours in BII (pH 7) (Graph 1). Moreover, dye coloration intensity reduction could even be vi- sually observed over time. Sealapex is an endodontic cement, with a cal- cium hydroxide base containing zinc oxide and reducing agents, and is able to decolorize methy- lene blue.13 Oztan et al.7 (2001) observed MB OD increase after contact with Sealapex specimens. In the present study, the Sealapex group promoted also significant OD increase in contact with MB and RB (Graph 1). The Sealapex group with BII reduced the dye OD values and visually presented a reduction in coloration intensity over time. Similar results were obtained by Oztan et al.7 (2001), who observed OD reduction in black India ink when in contact with specimens filled with Sealapex. Dyes or radioisotopes are used in 82% of mar- ginal leakage studies.11 However, since diffusion and dye coloration through the tooth/obturation material interface can be influenced by the interac- tion between obturation material, dye and dental structure, it is necessary to analyze the dental filling material influence on the optical density of the dye used in marginal leakage testing.5,13 It was observed that an assorted sample of dental filling materials changed dye OD (Graph 1). OD evaluation seems to be an interesting method to select the best dye solu- tion to use in a given marginal leakage study. Conclusions Considering the immersion effect of the evalu- ated materials on the OD of the three dyes tested, it was observed that: There was no significant statistical difference among the OD values of the three dye solutions evaluated, for each analysis period, when the AH Plus cement was evaluated. An immersion time longer than 24 hours is recommended; Portland cement promoted different OD values after 12 hours of immersion, in all of the three dyes evaluated. After 24 hours, there was differ- ence only for BII. Its use is recommended with MB and RB with an immersion period longer than 24 hours; MTA-Angelus cement presented different OD values only for RB, so its use is recommended with MB and BII at any time interval; MTA-Pro Root cement presented different OD values in all periods with the RB dye and up to 12 hours with the MB dye. BII is recommended for any period of time after 24 hours; Sealapex cement promoted a significant increase of the OD values for MB and RB and a decrease of the OD values of BII, when immersed for 48 and 72 hours. Therefore its use is recommended with BII for 12 and 24 hours. Acknowledgements This research was supported by the FUNDUNE- SP, PROINTER, PROPP program, grant 068/2003. MTA-Angelus was kindly donated by Mr. Paulo Sant’Anna. We also wish to thank Flávia S. Miyas- hira-Kubo for her assistance in manuscript prepara- tion. 1. 2. 3. 4. 5. References 1. Tamse A, Katz A, Kablan F. Comparison of apical leakage shown by four different dyes with two evaluating methods. Int Endod J. 1998;31(5):333-7. 2. Ahlberg KM, Assavanop P, Tay WM. A comparison of the apical dye penetration patterns shown by methylene blue and india ink in root-filled teeth. Int Endod J. 1995;28(1):30-4. The effect of endodontic materials on the optical density of dyes used in marginal leakage studies Braz Oral Res 2008;22(1):25-3030 3. Gale MS, Darvell BW. Controlling dentine penetration in com- puter microleakage tracer mapping. J Dent. 1997;25(2):129- 36. 4. Xavier CB, Weismann R, de Oliveira MG, Demarco FF, Po- zza DH. Root-end filling materials: apical microleakage and marginal adaptation. J Endod. 2005;31(7):539-42. 5. Vogt BF, Xavier CB, Demarco FF, Padilha MS. Dentin pen- etrability evaluation of three different dyes in root-end cavities filled with mineral trioxide aggregate (MTA). Braz Oral Res. 2006;20(2):132-6. 6. Torabinejad M, Watson TF, Pitt Ford TR. Sealing ability of a mineral trioxide aggregate when used as a root end filling material. J Endod. 1993;19(12):591-5. 7. Oztan MD, Ozgey E, Zaimoglu L, Erk N. The effect of various root canal sealers on India ink and different concentrations of methylene blue solutions. J Oral Sci. 2001;43(4):245-8. 8. Tanomaru Filho M, Figueiredo FA, Tanomaru JM. Effect of different dye solutions on the evaluation of the sealing ability of mineral trioxide aggregate. Braz Oral Res. 2005;19(2):119-22. 9. Kubo CH, Gomes AP, Mancini MN. In vitro evaluation of api- cal sealing in root apex treated with demineralization agents and retrofilled with mineral trioxide aggregate through mar- ginal dye leakage. Braz Dent J.2005;16(3):187-91. 10. Hamaoka L, Moura AAM. Avaliação in vitro da permeabilidade dentinária radicular, tendo como fonte de variação três diferentes tipos de corantes. Rev Odontol Univ São Paulo. 1996;10:39-42. 11. Wu MK, Wesselink PR. Endodontic leakage studies recon- sidered. Part I. Methodology, application and relevance. Int Endod J. 1993;26(1):37-43. 12. Youngson CC, Jones JC, Manogue M, Smith IS. In vitro den- tinal penetration by tracers used in microleakage studies. Int Endod J. 1998;31(2):90-9. 13. Wu MK, Kontakiotis EG, Wesselink PR. Decoloration of 1% methylene blue solution in contact with dental filling materi- als. J Dent. 1998;26(7):585-9. 14. Coffey S (ed.). Heterocyclic compounds. In: Rodd EH. Chem- istry of carbon compounds: a modern comprehensive treatise. 2nd ed. Amsterdam: Elsevier Scientific Publishing; 1978. 4H. p. 531-2. 15. Windholz M, Budavari S, Stroumtsos LY, Fertz MN. The Mer- ck Index. 9th ed. Rahway, NJ, USA: Merck & Co.; 1976. 16. Starkey DL, Anderson RW, Pashley DH. An evaluation of the effect of methylene blue dye pH on apical leakage. J Endod. 1993;19(9):435-9. 17. Lehninger AL, Nelson DL, Cox MM. A água e seus efeitos sobre as biomoléculas em solução. In: Lehninger AL, Nelson DL, Cox MM. Princípios de Bioquímica. 2ª ed. São Paulo: Sarvier; 1995. p. 61-78. 18. Estrela C, Bammann LL, Estrela CR, Silva RS, Pécora JD. Antimicrobial and chemical study of MTA, Portland cement, calcium hydroxide paste, Sealapex and Dycal. Braz Dent J. 2000;11(1):3-9. 19. Torabinejad M, Hong CU, McDonald F, Pitt Ford TR. Physical and chemical properties of a new root-end filling material. J Endod. 1995;21(7):349-53. 20. Holland R, de Souza V, Nery MJ, Otoboni Filho JA, Bern- abe PF, Dezan Junior E. Reaction of rat connective tissue to implanted dentin tubes filled with mineral trioxide aggregate or calcium hydroxide. J Endod. 1999;25(3):161-6. 21. Aqrabawi J. Sealing ability of amalgam, super EBA cement, and MTA when used as retrograde filling materials. Br Dent J. 2000;188:266-8.