Bull. Mater. Sci., Vol. 34, No. 6, October 2011, pp. 1213–1217. c© Indian Academy of Sciences. Electrical and microstructural properties of CaTiO3-doped K1/2Na1/2NbO3-lead free ceramics L RAMAJO∗, R PARRA, M A RAMÍREZ† and M S CASTRO Institute of Research in Materials Science and Technology (INTEMA), (CONICET – Universidad Nacional de Mar del Plata), Juan B Justo 4302 (B7608FDQ), Mar del Plata, Argentina †Faculdade de Engenharia de Guaratinguetá (FEG), Universidade Estadual Paulista (UNESP), Av. Dr. Ariberto Pereira da Cunha, 333, Bairro Pedregulho, CEP 12516-410, Guaratinguetá, SP, Brazil MS received 12 January 2011; revised 28 February 2011 Abstract. Microstructure, electrical properties and dielectric behaviour of K1/2Na1/2NbO3 (KNN) and CaTiO3- modified K1/2Na1/2NbO3 (CTO-KNN) systems, were investigated. Discs doped with 0 to 0·55% mol of CaTiO3 (CTO) were sintered at 1125◦C for 2 h. Although minority phases were found in doped samples, CaTiO3 was not detected. It was also observed that CTO changed the microstructure and grain size of KNN drastically. Also, the Curie temperature and permittivity values decreased. Addition of CTO between 0·15 and 0·45 mol% decreases the density and dielectric values. Samples prepared with higher content of CTO than 0·45 mol% showed better electrical properties. Keywords. Na0·5K0·5NbO3; CaTiO3; lead-free ceramics; electrical properties. 1. Introduction Lead zirconate titanate (PZT) ceramics are widely used in piezoelectric transducers, transformers and sensors due to their superior dielectric, ferroelectric and piezoelectric pro- perties (Du et al 2005; Yang et al 2005; Chang et al 2006). Nevertheless, due to the toxicity and its high vapour pressure during the sintering process, lead is a serious threat to human health and environment. Therefore, in recent years lead-free piezoelectric ceramics have attracted great attention. A number of researches on lead-free piezoelectric cera- mics such as alkaline niobiate (Saito et al 2004; Matsu- bara et al 2005), BaTiO3-based (Yu et al 2002), Bi-layered (Sawada et al 2003), bismuth sodium titanate (Zhou and Xin 2007; Zhou et al 2009) and tungsten bronze-type materials (Suzuki et al 2003) have been recently published. In this way, niobates (K,Na)NbO3 (KNN)-based ceramics have showed good piezoelectric and electric properties, high Curie tempe- rature and environmental innocuity (Maeder et al 2004; Wang et al 2004; Alkoy and Papila 2010). Also, when the ratio of K/Na reaches 50/50, the piezoelectric coefficient reaches the highest point (up to 80 pC/N) (Ringgaard and Wurlitzer 2005). Nevertheless, because of the high volati- lity of alkaline metals at high temperature and its hydrophilic feature, it is very difficult to obtain dense and well-sintered KNN ceramics using conventional sintering processes. A variety of modifications have been attempted to pre- pare new KNN-based ceramics with improved density and ∗Author for correspondence (lramajo@fi.mdp.edu.ar) piezoelectric properties, such as KNN–LiSbO3 (Tang et al 2007; Wang et al 2008) and KNN–LiNbO3 (Wu et al 2007). The improved piezoelectric properties of these ceramics could be due to the polymorphic phase transition (PPT) near or at room temperature (Bobnar et al 2004; Wang et al 2008; Wu et al 2008a), even though it has been found that these KNN systems possess low-temperature stability for PPT near to or at room temperature (Wu et al 2008b). This low- temperature stability restricts the practical applications of KNN-based ceramics. It would, therefore, be useful to obtain KNN-based ceramics with good temperature stability along with high piezoelectric properties for practical applications. In this work, K1/2Na1/2NbO3 (KNN) and CaTiO3–K1/2 Na1/2NbO3 (CTO–KNN) ceramics were prepared by a con- ventional sintering technique. The microstructure, dielectric and ferroelectric properties of these ceramics were studied. 2. Experimental Lead-free potassium sodium niobate, K1/2Na1/2NbO3 (KNN), was produced by the conventional solid state reac- tion method from potassium carbonate (Biopack 99·5%, Argentina), sodium carbonate (Cicarelli 99·7%, Argentina) and niobium oxide powder (Aldrich 99·9%, USA). Powders with K:Na = 1:1 and different CaTiO3 (CTO) concentrations (x = 0·15, 0·25, 0·45 and 0·55 mol%) were mixed and milled in 2-propanol in a planetary laboratory ball-mill (Fritsch, Pulverisette 5) with zirconia balls for 6 h at 1000 rpm using a ball-to-powder mass ratio of 7:10. Afterwards, the resulting powders were calcined at 900◦C for 5 h in air. 1213 1214 L Ramajo et al Powders were milled for a second time in a planetary labo- ratory ball-mill (Fritsch, Pulverisette 5) with zirconia balls for 30 min. This step reduced the particle size, which is nece- ssary to achieve a good dispersion and compaction. Then, the resulting powders were uniaxially pressed into discs of 6 mm in diameter and 0·5 mm in thickness. The obtained discs were sintered at 1125◦C for 180 min in a conventional fur- nace with 5◦C/min heating and cooling rates under ambient atmosphere. The crystalline phases were assessed by X-ray diffrac- tion using a Philips PW1050/25 diffractometer running with CuKα radiation, at 40 kV and 30 mA. The samples were examined by scanning electron microscopy (SEM), using a JEOL JSM-6460LV microscope. Silver electrodes were painted on the surface of the sin- tered samples for electrical measurements. Dielectric spec- troscopy measurements were carried out with a frequency response analyser HP 4284A LCR meter in the 20 Hz to 1 MHz frequency range. Polarization vs electric field hys- teresis loops were obtained at room temperature by apply- ing an electric field of sinusoidal waveform at a frequency of 50 Hz by means of a modified Sawyer–Tower bridge with the sample inside a silicone oil bath. 3. Results and discussion 3.1 XRD and SEM characterization Figure 1 shows the X-ray diffraction patterns of KNN doped with different concentrations of CTO (0 to 0·55 mol%) after sintering at 1125◦C for 120 min in air. The diffraction peaks could be clearly indexed to a perovskite with orthorhombic structure of KNN (Malic et al 2005; Birol et al 2006). Also, traces of secondary phases were detected, which could be (Na, K)Nb8O21 (Malic et al 2005) or other alkaline niobates like NaNb3O8 or K3NbO4 (JCPDS 84–1432 and 23–1345). CTO phase was not observed; probably due to problems to keep a stable structure inside KNN, since both have the same ABO3 perovskite structure, or due to homogeneous distribu- tion. Moreover, the addition of CTO induced a phase diffu- sion transition between an orthorhombic phase and a weak tetragonal phase. Figure 1(B) shows enlarged XRD patterns between 44·75 and 46·5. It can be seen that crystal structure of undoped KNN exhibited an orthorhombic structure with the splitting of (202) and (020) characteristic peaks at 2θ ∼ 45·5◦. How- ever, this phase decreases with increasing CTO content. In this way, the crystal structure of samples with higher dop- ing level revealed a clear evolution of the system toward a tetragonal structure. This phenomenon indicates that the orthorhombic and tetragonal phases coexist in KNN cera- mics with a small amount of CTO. The microstructural evolution of KNN as a function of CTO concentration is shown in the scanning electron microscopy images of figure 2. Undoped or doped samples Figure 1. XRD patterns of KNN undoped (0%) and 0·15 to 0·55 mol% CTO-doped samples. ( Secondary phases (A)). Inset shows magnified patterns in the 44·75 to 46·5 2θ range (B). with 0·15 mol% CTO exhibited similar grain size, shape and porosity, although both (size and shape) changed dramati- cally with increasing CTO content. Specimens with 0·25 and 0·45 mol% showed cubic, bigger grains with smooth faces. Additionally, these samples also presented lower density val- ues (table 1). On the other hand, specimens doped with 0·55 mol% showed higher density with elongated grains. 3.2 Dielectric and electric characterization NaNbO3 phase is known as an antiferroelectric perovskite- type compound and possesses many phase transitions between −100 and 643◦C. However, when it is combined with a ferroelectric phase like KNbO3, a new ferroelectric phase is produced with two phase transitions around 200 and 430◦C, corresponding to the transition temperatures of orthorhombic to tetragonal and tetragonal (ferroelectric) to cubic (paraelectric) phases, respectively (Chang et al 2007a). Electrical and microstructural properties of CaTiO3-doped K1/2Na1/2NbO3-lead free ceramics 1215 Figure 2. SEM images of undoped (A) and 0·15 (B), 0·25 (C), 0·45 (D) and 0·55 mol% (E) CTO-doped KNN samples. Table 1. Density (ρ), porosity, dielectric properties (εr, tan δ), Curie temperature (TC) and remnant polarization (Pr) of CTO doped KNN prepared by mixed oxide routes. Content of ρ Porosity εr tan (δ) TC Pr CTO (mol%) (g/cm3) (%) (at 10 kHz) (at 10 kHz) (◦C) (μC/cm2) 0·00 4·28 ± 0·1 5·47 ± 2·3 517·25 0·060 400 7·12 0·15 4·27 ± 0·1 5·51 ± 1·1 401·26 0·093 350 7·07 0·25 4·02 ± 0·1 12·76 ± 2·1 421·76 0·497 – – 0·45 3·99 ± 0·1 16·49 ± 6·9 434·34 0·201 – – 0·55 4·29 ± 0·1 5·06 ± 1·8 670·77 0·088 315 10·83 1216 L Ramajo et al Dielectric properties of KNN and CTO-doped KNN (0·15 and 0·55 mol%), as a function of temperature at 10 kHz are shown in figure 3. Pure KNN ceramics show two-phase transition temperatures: the orthorhombic–tetragonal poly- morphic phase transition (To−t) and the tetragonal–cubic ferroelectric–paraelectric phase transition (Curie tempera- ture, TC). It is observed that the transition temperatures and permittivity decrease when the CTO content is increased (Chu et al 2003; Chang et al 2006). Also, the real permi- ttivity peaks at TC were sharp and the highest values corre- spond to the undoped sample. Addition of 0·55 mol% shifted To−t close to room temperature. This phenomenon has been found in other compounds such as (Pb, La)(Zr, Ti)O3 and doped BaTiO3 (Guo et al 2004; Kosec et al 2004). It is suggested that a transition from a normal ferroelectric to ‘relaxor-like’ ferroelectric is due to the cation disorder in perovskite unit cell and the formation of microdomain since non-ferroelectric materials are added (Chang et al 2007b). (A) (B) Figure 3. Variation of (A) real part of permittivity and (B) loss tangent (tan δ) as a function of temperature of 0, 0·15 and 0·55 mol% CTO-doped KNN (at 10 kHz). It is known that the Curie temperature of CTO is nega- tive (Chandra et al 2006), and exhibits quantum paraelectric phase at room temperature or higher. In this way, in table 1, the real permittivity and loss tangent are shown at room temperature as a function of CTO concentration at 10 kHz. The lower real permittivity value belongs to samples doped with 0·15 mol% of CTO, after that it begins to increase. The loss tangent of CTO-doped KNN increases with increasing CTO content up to 0·45%mol, returning to values similar to undoped samples with a CTO concentration of 0·55 mol%. Finally, specimens with lowest porosity (0, 0·15 and 0·55 mol% of CTO), were analysed under an external strong electric field, exhibiting in all cases ferroelectric behaviour due to spontaneous polarization. Hysteresis loops of pure and doped-KNN with 0·15 and 0·55 mol% of CTO at room temperature under an a.c. electric field of Ep = 40 kV/cm at 50 Hz are shown in figure 4. Pure KNN shows a rem- nant polarization (Pr) of 7·12 μC/cm2, slightly higher than the value measured for the 0·15 mol% CTO doped-KNN, but lower than the measured one for the 0·55 mol% CTO doped-sample (7·07 and 10·83 μC/cm2, respectively). In this way, the coercive field Ec values of doped-KNN cera- mics with 0, 0·15 and 0·55 mol% of CTO are 15·8, 16·7 and 13·5 kV/cm and the higher saturation values (Ps) are 13·21, 12·96 and 16·54 μC/cm2, respectively. Pure and doped KNN with 0·15 mol% of CTO show almost equal standards due to the comparable grain size, microstructure, dielectric per- mittivity and density, while the 0·55 mol% doped-sample showed the highest values. This can be attributed to a diffuse phase transformation between an orthorhombic phase and a weak tetragonal phase, the higher dielectric permitivitty and average grain size of 0·55 mol% doped-KNN ceramic. Figure 4. Hysteresis loops of 0, 0·15 and 0·55 mol% CTO-doped KNN at room temperature. Measuring conditions: a.c. field, electric field of 40 kV/cm and frequency of 50 Hz. Electrical and microstructural properties of CaTiO3-doped K1/2Na1/2NbO3-lead free ceramics 1217 4. Conclusions The effect of CTO (0 to 0·55 mol %) on the microstruc- ture, phase transition and electric properties of KNN sys- tems prepared by the conventional mixed oxide method has been studied. X-ray diffraction patterns showed the forma- tion of a solid solution of CTO in KNN with perovskite-type structure. The average grain size, transition temperatures and real permittivity at room temperature were modified by the increasing CTO content. The temperature dependence of real permittivity revealed that the examined samples showed a diffuse phase transi- tion character and this character was more obvious with increasing concentration of CTO. Small additive quantized slightly modified the properties, even though highest values decreased density and electric properties up to CTO 0·45 mol%. After that, the properties (density, and real permittivity) improved up to values simi- lar to undoped ceramics. In this way, the results of this study suggest that KNN doped with 0·55 mol% of CTO would be a good candidate for ferroelectric devices. Acknowledgements The authors are grateful to CONICET and ANCyPT (Argentina) and to CNPq and FAPESP (Brasil) for the financial support provided for this research. References Alkoy E M and Papila M 2010 Ceram. Int. 36 1921 Birol H, Damjanovic D and Setter B 2006 J. Eur. Ceram. Soc. 26 861 Bobnar V, Bernard J and Kosec M 2004 Appl. Phys. Lett. 85 994 Chandra A, Ranjan R, Singh D P, Khare N and Pandey D 2006 J. Phys. Condens. Matter 18 2977 Chang R-C, Chu S-Y, Lin Y-F, Hong C-S, Kao P-C and Lu C-H 2007a Sensors Actuator A138 355 Chang R-C, Chu S-Y, Lin Y-F, Hong C-S and Wong Y-P 2007b J. Eur. Ceram. Soc. 27 4453 Chang Y, Yang Z, Wei L and Liu B 2006 Mater. Sci. Eng. A437 301 Chu S Y, Water W, Juang Y D, Liaw J T and Dai S B 2003 Ferroelectrics 287 23 Du H, Qu S, Che J, Liu Z, Wei X and Pei Z 2005 Mater. Sci. Eng. A393 36 Guo Y, Kakimoto K and Ohsato H 2004 Solid State Commun. 129 279 Kosec M, Bobnar V, Hrovat M, Bernard J, Malic B and Holc J 2004 J. Mater. Res. 19 1849 Maeder M D, Damjanovic D and Setter N 2004 J. Electroceram. 13 385 Malic B, Bernard J, Holc J, Jenko D and Kosec M 2005 J. Eur. Ceram. Soc. 25 2707 Matsubara M, Yamaguchi T, Sakamoto W, Kikuta K, Yogo T and Hirano S 2005 J. Am. Ceram. Soc. 88 1190 Ringgaard E and Wurlitzer T 2005 J. Eur. Ceram. Soc. 25 2701 Saito Y, Takao H, Tani T, Nonoyama T, Takatori K, Homma T, Nagaya T and Nakamura M 2004 Nature 432 84 Sawada T, Ando A, Sakabe Y, Damjanovic D and Setter N 2003 Jpn. J. Appl. Phys. 42 6094 Suzuki M, Nagata H, Ohara J, Funakubo H and Takenaka T 2003 Jpn. J. Appl. Phys. 42 6090 Tang F S, Du H L, Liu D J, Luo F and Zhou W C 2007 J. Inorg. Mater. 22 0323 Wang K, Li J and Liu N F 2008 Appl. Phys. Lett. 93 092904 Wang X, Kwork K, Tang X, Chan H and Choy Z 2004 Solid State Commun. 129 319 Wu J G, Xiao D, Wang Y, Zhu J, Yu P and Jiang Y 2007 J. Appl. Phys. 102 114113 Wu J G, Xiao D Q, Wang Y Y, Zhu J G and Yu P 2008a J. Appl. Phys. 103 024102 Wu J, Xiao D, Wang Y, Wu W, Zhang B, Li J and Zhu J 2008b Scr. Mater. 59 750 Yang Z P, Chang Y F and Li H 2005 Mater. Res. Bull. 40 2110 Yu Z, Ang C, Guo R and Bhalla A S 2002 J. Appl. Phys. 92 1489 Zhou C-H and Xin X-Y 2007 Bull. Mater. Sci. 30 575 Zhou C-H, Liu X-Y, Li W-Z and Yuan C-L 2009 Bull. Mater. Sci. 32 99 Electrical and microstructural properties of CaTiO3-doped K1/2Na1/2NbO3-lead free ceramics Abstract Introduction Experimental Results and discussion XRD and SEM characterization Dielectric and electric characterization Conclusions References