Casas-Apayco, Leslie CarollDreibi, Vanessa ManziniHipolito, Ana Carolina [UNESP]Zardin Graeff, Marcia SirleneRios, DanielaMagalhaes, Ana CarolinaRabelo Buzalaf, Marlia AfonsoWang, Linda2015-11-032015-11-032014-09-01Journal Of Applied Oral Science. Bauru-sp: Univ Sao Paulo Fac Odontologia Bauru, v. 22, n. 5, p. 434-441, 2014.1678-7757http://hdl.handle.net/11449/129944Objective: This study aimed to assess the impact of in vitro erosion provoked by different cola-based drinks (Coke types), associated or not with toothbrushing, to bonding to enamel. Material and Methods: Fifty-six bovine enamel specimens were prepared and randomly assigned into seven groups (N=8): C-Control (neither eroded nor abraded), ERO-RC: 3x/1-min immersion in Regular Coke (RC), ERO-LC: 3x/1-min immersion in Light Coke (LC), ERO-ZC: 3x/1-min immersion in Zero Coke (ZC) and three other eroded groups, subsequently abraded for 1-min toothbrushing (EROAB-RC, EROAB-LC and EROAB-ZC, respectively). After challenges, they were stored overnight in artificial saliva for a total of 24 h and restored with Adper Single Bond 2/Filtek Z350. Build-up coronal surfaces were cut in 1 mm(2)-specimens and subjected to a microtensile test. Data were statistically analyzed by two-way ANOVA/Bonferroni tests (alpha=0.05). Failure modes were assessed by optical microscopy (X40). The interface of the restorations were observed using Confocal Laser Scanning Microscopy (CLSM). Results: All tested cola-based drinks significantly reduced the bond strength, which was also observed in the analyses of interfaces. Toothbrushing did not have any impact on the bond strength. CLSM showed that except for Zero Coke, all eroded specimens resulted in irregular hybrid layer formation. Conclusions: All cola-based drinks reduced the bond strength. Different patterns of hybrid layers were obtained revealing their impact, except for ZC.434-441engTooth abrasionBonding agentEnamelErosionSoft drinksArtigo10.1590/1678-775720130468S1678-77572014000500434WOS:000345917200012Acesso abertoS1678-77572014000500434.pdf