Souza, A. E. [UNESP]Santos, G. T. A. [UNESP]Barra, B. C. [UNESP]Macedo, W. D. [UNESP]Teixeira, S. R. [UNESP]Santos, C. M.Senos, A. M. O. R.Amaral, L.Longo, Elson [UNESP]2014-05-202014-05-202012-11-01Crystal Growth & Design. Washington: Amer Chemical Soc, v. 12, n. 11, p. 5671-5679, 2012.1528-7483http://hdl.handle.net/11449/6901SrTiO3 crystalline nanoparticles were prepared using the microwave-assisted hydrothermal method at 140 degrees C with synthesis times varying from 4 to 160 min. Sample characterization showed that the method is effective in obtaining nanoparticles in a relatively short time, which have the highest photoluminescence emission. The crystalline phase of perovsldte-typer SrTiO3 is not significantly influenced by synthesis time However, the SrTiO3 phase is already obtained with a 4 min synthesis time Also, all samples exhibited photoluminescence at room temperature in the blue-green region, where intensity decreased with increasing synthesis time and particle size. The samples synthesized with the shortest time showed higher photoluminescence emission and smaller particle sizes. The morphology, obtained based on FE-SEM showed cubic nanoparticles with inhomogeneous grain growth at higher temperatures of synthesis in addition to the formation of new architectures.5671-5679engArtigo10.1021/cg301168kWOS:000311240100063Acesso restrito9256541983393135