Xavier, Camila S.Candeia, R. A.Bernardi, M. I. B.Lima, S. J. G.Longo, Elson [UNESP]Paskocimas, C. A.Soledade, L. E. B.Souza, A. G.Santos, Ieda M. G.2014-05-202014-05-202007-03-01Journal of Thermal Analysis and Calorimetry. Dordrecht: Springer, v. 87, n. 3, p. 709-713, 2007.1388-6150http://hdl.handle.net/11449/37832Magnesium and zinc ferrites have been prepared by the polymeric precursor method. The organic material decomposition was studied by thermogravimetry (TG) and differential thermal analysis (DTA). The variation of crystalline phases and particle morphology with calcination temperature were investigated using X-ray diffraction (XRD) and scanning electronic microscopy (SEM), respectively. The colors of the ferrites were evaluated using colorimetry. Magnesium ferrite crystallizes above 800 degrees C, presenting a yellow-orange color with a reflectance peak at the 600-650 nm range, while zinc ferrite crystallizes at 600 degrees C, with a reflectance peak between 650-700 nm, corresponding to the red-brick color.709-713engmagnesium ferritePechinithermal analysiszinc ferriteArtigo10.1007/s10973-006-7744-6WOS:000244823700019Acesso restrito