Efeitos do envelhecimento acelerado artificial nas propriedades ópticas de resinas compostas
Nenhuma Miniatura disponível
Data
2018-03-01
Autores
Dantas, Débora Cristina Barbosa [UNESP]
Mathias, Ingrid Fernandes [UNESP]
Borges, Alessandra Bühler [UNESP]
Torres, Carlos Rocha Gomes [UNESP]
Caneppele, Taciana Marco Ferraz [UNESP]
Título da Revista
ISSN da Revista
Título de Volume
Editor
Resumo
The aim of this study was to evaluate the effects of ultraviolet artificial aging on color, fluorescence, gloss, and translucency of different composite resins. Seventy-five cylindrical-shaped specimens (6 mm in diameter and 1 mm thick) of four different composites: Admira Fusion (VOCO), TPH3 (DENTSPLY), GrandioSO (VOCO) and Filtek™ Z350 XT (3M/ESPE), were built. Enamel samples obtained from bovine incisors were prepared with the same dimensions and used as a control group. Assessments of color, translucency, fluorescence, and gloss were performed at baseline and after artificial aging. Specimens were immersed in artificial saliva and submitted to artificial aging (UV light for 300h). Data were analyzed using one-way ANOVA and Tukey’s post hoc test (α=0.05). After aging, all resin composites presented significant alterations, mainly Filtek™ Z350 XT. Fluorescence decreased in all resin composites and enamel. Gloss was reduced in all groups, too, with major rates for TPH3 and GrandioSO, which was similar to the enamel reduction. Translucency did not present a significant difference for the resin composites, although there was a reduction in the enamel. After artificial aging resin composites became darker, less fluorescent, less glossy, and with no alteration in translucency.
Descrição
Palavras-chave
Aging, Color, Composites, Enamel, Fluorescence, Gloss, Translucency
Como citar
Bioscience Journal, v. 34, n. 2, p. 1105-1113, 2018.