Dielectric Behavior of alpha-Ag2WO4 and its Huge Dielectric Loss Tangent
Carregando...
Data
2019-01-01
Autores
Jacomaci, Natalia [UNESP]
Silva Junior, Euripedes [UNESP]
Borges de Oliveira, Fernando Modesto
Longo, Elson
Zaghete, Maria Aparecida [UNESP]
Título da Revista
ISSN da Revista
Título de Volume
Editor
Univ Fed Sao Carlos, Dept Engenharia Materials
Resumo
The microwave-assisted hydrothermal method was used to obtain alpha-Ag2WO4. Rietveld refinement confirmed that alpha-Ag2WO4 is stable in the orthorhombic phase, without secondary phase. However, field-effect scanning electron microscope analysis showed that alpha-Ag2WO4 nanorods surfaces contain silver nanoparticles, confirmed by the X-ray photoelectron spectroscopy by the peak observed at 374.39 eV In addition to metallic Ag, other Ag oxidation states were also observed on the surface. Hence, Ag (I) as Ag2O and Ag (I) as Ag(2)WO(4 )also were identified. DC measurements exhibited a high capacity of charge storage, nevertheless, with a large loss tangent (0.12 mu C.cm(-2).V-1) and no residual polarization for the voltage range between -100 V and +100 V. AC measurements at frequencies less than 275 Hz, revealed that ionic polarization is dominant, whereas at frequencies higher than 275 Hz, the electronic behavior predominates. The potential of electromagnetic energy conversion in thermal was observed from loss tangent analysis.
Descrição
Palavras-chave
Silver tungstate nanorods, dielectric behavior, ionic and electronic polarization
Como citar
Materials Research-ibero-american Journal Of Materials. Sao Carlos: Univ Fed Sao Carlos, Dept Engenharia Materials, v. 22, n. 4, 10 p., 2019.