Use of sonic waves in bubble formation, microhardness and fluoride release of a high-viscosity glass-ionomer cement
Nenhuma Miniatura disponível
Data
2019-11-01
Autores
Lima Hironaka, Nallu Gomes
Trizzi, Juliana Quintino [UNESP]
Yoshida, Natalia Miwa
Cury, Jaime Aparecido
Machado Tabchoury, Cinthia Pereira
Botelho, Juliana Nunes
Pini, Nubia Inocencya Pavesi
Pascotto, Renata Correa
Título da Revista
ISSN da Revista
Título de Volume
Editor
Wiley-Blackwell
Resumo
Aim High-viscosity glass-ionomer cements (HV-GIC) are indicated for restorations but their viscosity favors the inclusion of bubbles within it. This study aimed to evaluate the use of ultrasonic and sonic waves in bubble formation, microhardness and fluoride release in a HV-GIC, also considering a different powder:liquid ratio (P/L). Methods Twenty-four molars with occlusal cavities were divided into four groups (N = 6): CG, HV-GIC with manual insertion; UG, application of ultrasonic waves; SG, application of sonic waves; and FG, HV-GIC fluid (1:2 P/L) with manual insertion. After 24 hours, bubbles and microhardness (50 g/5 s) were measured. Fluoride release (N = 10) was evaluated in CG, SG and UG after cariogenic challenge for 11 days. Microhardness, total area and number of bubbles, and fluoride release were submitted to ANOVA and Tukey's test. The average size of bubbles was analyzed by Kruskal-Wallis test (alpha = 5%). Results FG presented the lowest value of microhardness and higher average size for bubbles (P < .05). Differences concerning total number, total area occupied by bubbles and fluoride release were not found (P > .05). Conclusion The use of sonic and ultrasonic waves had no influence on bubble formation, microhardness and fluoride release of a HV-GIC. Changing the P/L is not recommended.
Descrição
Palavras-chave
fluorides, glass-ionomer cement, microhardness
Como citar
Journal Of Investigative And Clinical Dentistry. Hoboken: Wiley, v. 10, n. 4, 8 p., 2019.