Fabrication of fish gelatin microfibrous mats by solution blow spinning
Carregando...
Data
2019-01-01
Autores
Vilches, José Luiz [UNESP]
De Souza Filho, Men De Sá Moreira
De Freitas Rosa, Morsyleide
Sanches, Alex Otávio [UNESP]
Malmonge, José Antonio [UNESP]
Título da Revista
ISSN da Revista
Título de Volume
Editor
Resumo
In this work microfiber mats of Nile tilapia (Oreochromis niloticus) gelatin were successfully fabricated by using Solution Blow Spinning technique. The concentration and viscosity of fish gelatin solution, in acid acetic/water (80% v/v), were correleted to the morphology and diameter of the gelatin microfibers. It was found that increased solution viscosity leads to increase of fibers diameters from approximately 280 nm at viscosity ~ 0.085 Pa.s. to approximately 1195 nm at viscosity ~ 1.877 Pa.s. The TG thermograms showed similar thermal profiles for all fibrous mat gelatins with thermal stability at temperatures below 180°C. The DSC curve showed two endothermic peaks being the second one, in the range of 100-130°C, strongly influenced by the microfiber diameters. It shifts to higher temperature increasing the microfiber diameter. This behavior was associated to the diffusion of water in the microfibers. Combined DSC/TG results showed a significant influence of the microfiber diameter on the water absorption and desorption process.
Descrição
Palavras-chave
Fish gelatin, Gelatin microfiber, Nile tilapia, Solution blow spinning
Como citar
Materials Research, v. 22.