Structure study of Bi4Ti3O12 produced via mechanochemically assisted synthesis
Nenhuma Miniatura disponível
Data
2008-07-01
Autores
Stojanovic, Biljana D. [UNESP]
Paiva-Santos, Carlos O. [UNESP]
Cilense, Mario [UNESP]
Jovalekic, Cedomir
Lazarevic, Zorica Z.
Título da Revista
ISSN da Revista
Título de Volume
Editor
Pergamon-Elsevier B.V. Ltd
Resumo
Nanosized bismuth titanate was prepared via high-energy ball milling process through mechanically assisted synthesis directly from their oxide mixture of Bi2O3 and TiO2. Only Bi4Ti3O12 phase was formed after 3 h of milling time. The excess of 3 wt% Bi2O3 added in the initial mixture before milling does not improve significantly the formation of Bi4Ti3O12 phase comparing to stoichiometric mixture. The formed phase was amorphized independently of the milling time, The Rietveld analysis was adopted to determine the crystal structure symmetry, amount of amorphous phase, crystallite size and microstrains. With increasing the milling time from 3 to 12 h, the particle size of formed Bi4Ti3O12 did not reduced significantly. That was confirmed by SEM and TEM analysis. The particle size was less than 20 nm and show strong tendency to agglomeration. The electron diffraction pattern indicates that Bi4Ti3O12 crystalline powder is embedded in an amorphous phase of bismuth titanate. Phase composition and atom ratio in BIT ceramics were determined by X-ray diffraction and EDS analysis. (c) 2007 Elsevier Ltd. All rights reserved.
Descrição
Palavras-chave
ceramics, nanostructures, electron microscopy, X-ray diffraction, crystal structure
Como citar
Materials Research Bulletin. Oxford: Pergamon-Elsevier B.V. Ltd, v. 43, n. 7, p. 1743-1753, 2008.