Yellow ZnxNi1-xWO4 pigments obtained using a polymeric precursor method
Nenhuma Miniatura disponível
Data
2008-01-01
Autores
de Oliveira, Andre Luiz M.
Ferreira, Jailson M.
Silva, Marcia R. S.
Braga, Glauco S.
Soledade, Luiz E. B.
Maurera Maria Aldeiza, M. A.
Paskocimas, Carlos A.
Lima, Severino J. G.
Longo, Elson [UNESP]
de Souza, Antonio Gouveia
Título da Revista
ISSN da Revista
Título de Volume
Editor
Elsevier B.V.
Resumo
New tungstate-based ceramic pigments, displaying ZnxNi1-xWO4 stoichiometry, were obtained at low temperature using a polymeric precursor method. The powder precursors were milled in an attritor mill in an alcoholic rnedium and heat treated for 12 h. yielding homogeneous and crystalline powder pigments. Characterization (TG/DTA, XRD, IR and colorimetry) showed that mass loss increased with increasing Zn contents. Despite the presence of secondary phases and impurities, the wolframite phase was present in all samples. IR analysis revealed bands related to Me-O and [WO6](6-) group stretching was observed. The intensity of the yellow color of the pigments increased with increasing amount of nickel. (c) 2007 Elsevier Ltd. All fights reserved.
Descrição
Palavras-chave
wolframite, yellow pigments, tungstate, absorbance, colorimetry
Como citar
Dyes and Pigments. Oxford: Elsevier B.V., v. 77, n. 1, p. 210-216, 2008.