BaMoO4:Tb3+ phosphor properties: Synthesis, characterization and photophysical studies

Nenhuma Miniatura disponível

Data

2011-11-02

Autores

Marques, Ana Paula A.
Motta, Fabiana V.
Cruz, Mariana A.
Varela, José Arana [UNESP]
Longo, Elson [UNESP]
Rosa, Ieda L. V.

Título da Revista

ISSN da Revista

Título de Volume

Editor

Elsevier B.V.

Resumo

BaMoO4:Tb3+ powders were synthesized by the complex polymerization (CP) method and characterized by powder X-ray diffraction patterns (XRD), Fourier transform infra-Red (FTIR) and Raman spectroscopy as well as photoluminescence (PL) measurements. The results confirmed the presence of a crystalline scheelite-type phase in BaMoO4:TP3+ crystalline powers. Excitation spectra, lambda(em).= 543 nm revealed the predominance of a broad band of charge transfer that was ascribed to the absorption of [MoO4](2-) ionic tetragonal clusters. Emission spectra of BaMoO4:Tb3+ samples (lambda(ex.)= 294 nm) have a group of sharp emission bands (456-487 nm; 543-546 nm; 581-589 nm and 617-620 nm) assigned to the D-5(4) -> F-7(6), D-5(4) -> F-7(5), D-5(4) -> F-7(4) and D-5(4) -> F-7(3) transitions of Tb3+ ions, respectively. The samples show the exponential decay curves of D-5(4) -> F-7(5) transition, lambda(exc). = 294 nm and lambda(em) = 543 nm, where the greater decay time was evaluated as 1.07 ms for the BaMoO4:Tb3+ annealed at 900 degrees C. (C) 2011 Elsevier B.V. All rights reserved.

Descrição

Palavras-chave

Molybdate, Complex polymerization method, Luminescence, Tb3+ doped

Como citar

Solid State Ionics. Amsterdam: Elsevier B.V., v. 202, n. 1, p. 54-59, 2011.