Preparation of Ni-Ti-Mo and Ni-Ti-Mo-Zr Alloys by High-Energy Ball Milling and Subsequent Hot Pressing
Nenhuma Miniatura disponível
Data
2012-01-01
Autores
Cortez Pereira, Gilda Maria [UNESP]
de Souza, Marisa Aparecida [UNESP]
Hashimoto, Tomaz Manabu [UNESP]
Rodrigues Henriques, Vinicius Andre
Ramos, Alfeu Saraiva [UNESP]
Título da Revista
ISSN da Revista
Título de Volume
Editor
Trans Tech Publications Ltd
Resumo
This work discusses on the preparation of Ni-45Ti-5Mo, Ni-40Ti-10Mo and Ni-46Ti-2Mo-2Zr (at-%) alloys by high-energy ball milling and hot pressing, which are potentially attractive for dental and medical applications. The milling process was performed in stainless steel balls (19mm diameter) and vials (225 mL) using a rotary speed of 300rpm and a ball-to-powder weight ratio of 10:1. Hot pressing under vacuum was performed in a BN-coated graphite crucible at 900 degrees C for 1 h using a load of 20 MPa. The milled and hot-pressed materials were characterized by X-ray diffraction, electron scanning microscopy, and electron dispersive spectrometry. Peaks of B2-NiTi and Ni4Ti3 were identified in XRD patterns of Ni-45Ti-5Mo, Ni-40Ti-10Mo and Ni-46Ti-2Mo-2Zr powders milled for 1h. The NiTi compound dissolved small Mo amounts lower than 4 at%, which were measured by EDS analysis. Moreover, it was identified the existence of an unknown Mo-rich phase in microstructures of the hot-pressed Ni-Ti-Mo alloys.
Descrição
Palavras-chave
amorphous, mechanical alloying, nickel alloys, nitinol
Como citar
Advanced Powder Technology Viii, Pts 1 and 2. Stafa-zurich: Trans Tech Publications Ltd, v. 727-728, p. 233-238, 2012.