Dispositivos funcionais de ZIF-8 e ZnO derivado de ZIF-8

Página do item simplificado
dc.contributor.advisorBufon, Carlos Cesar Bof [UNESP]
dc.contributor.authorFingolo, Ana Claudia
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2022-03-31T16:38:38Z
dc.date.available2022-03-31T16:38:38Z
dc.date.issued2022-03-25
dc.description.abstractAs Estruturas Metalorgânicas (MOF, do inglês Metal Organic Framework) são compostos que tem atraído bastante atenção nas últimas décadas devido as suas características de alta porosidade, cristalinidade e versatilidade pois apresentam amplas possibilidades de funcionalização. Um exemplo de destaque desta classe é o ZIF-8 formado por íons zinco e o ligante 2-metilimidazol. Este material apresenta alta estabilidade química, além das características comuns dos MOFs. Quando aquecido acima de ~450 °C, a oxidação dos íons Zn do ZIF-8 gera ZnO com alta porosidade devido a estrutura do precursor, enquanto a degradação do ligante orgânico leva a formação de uma matriz de carbono condutor. A presença do carbono condutor pode melhorar as propriedades elétricas deste material resultante, o que pode auxiliar em diversas aplicações deste semicondutor. Por este motivo, neste trabalho foram testados três métodos para a formação de ZnO derivado de ZIF-8 de forma localizada, com boa resolução espacial, visando sua aplicação em dispositivos baseados em filmes finos. Os métodos utilizados foram: a Oxidação Anódica Local, utilizando um microscópio de AFM, o tratamento com laser acoplado a um espectrômetro Raman e o tratamento térmico baseado no Efeito Joule em dispositivos fabricados usando técnicas de microfabricação e deposição de filmes finos. A estrutura cristalina dos filmes depositados foi avaliada por DRX, confirmando a formação de ZIF-8. Após o tratamento térmico, houve um grande encolhimento da estrutura, como visto em imagens de topografia obtidas por AFM. Os grupos funcionais presentes no filme também sofreram mudanças, como observado por espectroscopia Raman, com o surgimento de dois picos característicos do ZnO. Foi observada uma grande mudança no comportamento elétrico dos filmes, com um aumento de pelo menos cinco ordens de grandeza na corrente máxima alcançada em curvas I vs V de 0 a 2 V realizadas em um analisador de semicondutores.pt
dc.description.abstractMetal Organic Frameworks (MOF) are a class of materials that have attracted great attention in recent decades due to its characteristic’s high porosity, crystallinity, and versatility with wide possibilities of functionalization. These compounds are formed by a metallic center, composed of an ion or cluster, coordinated to organic ligands. A prominent example of this class is ZIF-8, which is formed by zinc ions and 2-methylimidazole as ligand. This material has high chemical and physical stability in addition to the most common characteristics of MOFs. When heated above ~450 °C, Zn ions oxidation leads to ZnO formation, with high porosity due to precursor structure, while organic ligand degradation leads to a conductive carbon matrix formation. Conductive carbon presence can improve the electrical properties of the resulting material, which can be an advantage in several applications of this semiconductor. In this work, three methods for the formation of ZnO derived from ZIF-8 with spatial resolution were tested, aiming its application in thin-film-based devices. The treatment methods were: Local Anodic Oxidation (LAO) using an atomic force microscope (AFM), laser treatment coupled to a Raman spectrometer and thermal treatment based on Joule Heating on devices manufactured by photolithography. The films’ crystalline structure was analyzed by XRD, and the formation of ZIF-8 was confirmed. After thermal treatment a large structure shrinkage was observed in topography images obtained by AFM. The functional groups present in the films suffered changes as observed through Raman spectroscopy. After treatment two peaks belonging to ZnO were seen. Electrical behavior of the films was compared before and after thermal treatment using a semiconductor analyzer and a probe station. An increase of at least five orders of magnitude was observed for the maximum current obtained in IvsV curves from 0 to 2V.en
dc.identifier.capes33004056083P7
dc.identifier.urihttp://hdl.handle.net/11449/217547
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.subjectEstruturas organicas metálicas (MOF)pt
dc.subjectFilmes finospt
dc.subjectMateriais nanoestruturadospt
dc.subjectThin-filmsen
dc.subjectZIF-8 derived ZnOen
dc.subjectNanodevicesen
dc.titleDispositivos funcionais de ZIF-8 e ZnO derivado de ZIF-8pt
dc.title.alternativeZIF-8 and ZIF-8 derived ZnO functional devicesen
dc.typeDissertação de mestrado
unesp.campusUniversidade Estadual Paulista (Unesp), Faculdade de Ciências, Baurupt
unesp.embargoOnlinept
unesp.examinationboard.typeBanca públicapt
unesp.graduateProgramCiência e Tecnologia de Materiais - FCpt
unesp.knowledgeAreaMateriaispt
unesp.researchAreaMateriais Poliméricos, Cerâmicos, Híbridos, e Nano Estruturaispt

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
fingolo_ac_me_bauru.pdf
Tamanho:
5.57 MB
Formato:
Adobe Portable Document Format
Descrição:
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Nenhuma Miniatura disponível
Nome:
license.txt
Tamanho:
2.94 KB
Formato:
Item-specific license agreed upon to submission
Descrição:

Coleções

Dissertações - Ciência e Tecnologia de Materiais - FC