Efeito dos parâmetros de pulso sobre as características geométricas e desempenho da soldagem com arame tubular autoprotegido e corrente pulsada

Página do item simplificado
dc.contributor.advisorKobayashi, Yukio [UNESP]
dc.contributor.authorCorrêa, Fábio Ricardo Torrano [UNESP]
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2014-06-11T19:28:21Z
dc.date.available2014-06-11T19:28:21Z
dc.date.issued2006-01-20
dc.description.abstractNo presente trabalho buscou-se determinar o comportamento das características geométricas do cordão da solda e o desempenho da soldagem, através do processo de soldagem com arame tubular autoprotegido e corrente pulsada. As características geométricas estudadas foram largura do cordão, penetração da solda e altura do reforço. Para definir o desempenho da soldagem analisou-se o rendimento de deposição e a taxa de deposição. Como metal de base utilizou-se o aço ABNT 1010 de espessura 6,35mm. O arame utilizado foi o AWS E71T-11 com diâmetro 1,1mm. A soldas foram realizadas por simples deposição, utilizando-se uma fonte de solda microprocessada, mantendo-se a velocidade de soldagem e a distancia tocha/peça constante. Durante o processo de soldagem os parâmetros de pulso analisados foram a corrente de pico (Ap), corrente de base (Ab), freqüência de pulso (F) e tempo de pico (Tp). Para coleta dos dados foi utilizada uma placa de aquisição de dados com interface a um microcomputador. De posse dos dados, foi aplicada a técnica de ANOVA, com o objetivo de identificar, quantificar e localizar a significância das dispersões. Verificou-se que a tensão média tem grande influência nas características geométricas do cordão de solda e de desempenho da soldagem. Para cada incremento de F provocou uma redução da largura do cordão de solda e aumento da penetração, altura do reforço, taxa de deposição e rendimento de deposição. O incremento Tp acarretou a formação de cordões mais largos, como também a redução na altura do reforço, penetração, taxa de deposição e rendimento de deposição. A variação de Ap não teve influência sobre largura do cordão, a altura do reforço, taxa de deposição e rendimento de deposição.pt
dc.description.abstractIn the present work one searched to determine the behavior of the geometric characteristics of the bead weld and the performance of the welding, through the process self-shielded flux cored arc welding and pulsed current. The studied geometric characteristics had been width of bead, penetration of the weld, height of the reinforcement. To define the performance of the welding one analyzed the deposition efficiency and the deposition rate. As metal base was used steel ABNT 1010 with thickness 6, 35 mm. The used wire was the AWS E71T-11 with diameter 1,1 mm. The welds had been carried through by simple deposition, using themselves a microprocessed weld power source, remaining constant it welding speed and the stick-out. During the welding process the analyzed parameters of pulse had been the peak current (Ap), base current (Ab), pulse frequency (F) and peak duration (Tp). For collection of the data a plate of acquisition of data with interface to a microcomputer was used. Of ownership of the data, the ANOVA technique was applied, with the objective to identify, to quantify and to locate the significance of the dispersions. It was verified that the mean voltage has great influence in the geometric characteristics of the bead weld and the performance of the welding. For each increment of F it provoked a reduction of the width of the bead weld and increase of the penetration, height of the reinforcement, deposition rate and deposition efficiency. The Tp increment caused the wider bead weld formation, as also the reduction in the height of the reinforcement, penetration, deposition rate and deposition efficiency. The variation of Ap did not have influence on width of the bead weld, the height of the reinforcement, deposition rate and deposition efficiency.en
dc.format.extent105 f. : il.
dc.identifier.aleph000456182
dc.identifier.capes33004056080P8
dc.identifier.citationCORRÊA, Fábio Ricardo Torrano. Efeito dos parâmetros de pulso sobre as características geométricas e desempenho da soldagem com arame tubular autoprotegido e corrente pulsada. 2006. 105 f. Dissertação (mestrado) - Universidade Estadual Paulista, Faculdade de Engenharia, 2006.
dc.identifier.filecorrea_frt_me_bauru.pdf
dc.identifier.lattes4098511928890053
dc.identifier.urihttp://hdl.handle.net/11449/96497
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.sourceAleph
dc.subjectSoldagempt
dc.subjectEngenharia mecanicapt
dc.subjectArame tubular autoprotegidopt
dc.subjectCaracterísticas geométricaspt
dc.subjectGeometric characteristicsen
dc.titleEfeito dos parâmetros de pulso sobre as características geométricas e desempenho da soldagem com arame tubular autoprotegido e corrente pulsadapt
dc.typeDissertação de mestrado
unesp.author.lattes4098511928890053
unesp.campusUniversidade Estadual Paulista (Unesp), Faculdade de Engenharia, Baurupt
unesp.graduateProgramEngenharia Mecânica - FEBpt
unesp.knowledgeAreaProcessos de fabricaçãopt

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
correa_frt_me_bauru.pdf
Tamanho:
1.26 MB
Formato:
Adobe Portable Document Format
Baixar

Coleções

Dissertações - Engenharia Mecânica - FEB